The effects of high concentration tooth whitening bleaches on microleakage of Class V composite restorations.

Objective: To explore the effects of high-concentration hydrogen peroxide bleaching agents on the microleakage of composite restorations.

Methods: In 60 extracted human molars, Class V restorations were prepared with Scotchbond 1/Filtek Z250 composite. Teeth were randomly divided into four groups: (1) no bleaching; (2) bleaching with 14% hydrogen peroxide gel from Crest Whitestrips; (3) bleaching with 20% carbamide peroxide gel from Opalescence PF 20; and (4) bleaching with 38% hydrogen peroxide gel Opalescence Xtra Boost. Bleaching procedures were carried out at 37 degrees C for 21 days/42 hours (2); seven days/42 hours (3); one day/45 minutes (4). Varnish was applied on the apical portion of the teeth only, excluding the restoration, prior to immersion in a 0.1% rhodamin-B-isothiocyanate solution for 24 hours at 37 degrees C. After rinsing, specimens were embedded in methacrylate blocks, and sectioned with a water-cooled microtome with three restoration cuts positioned centrally parallel to the long axis of the tooth. Microleakage was evaluated at the occlusal margins of the Class V restorations using a stereo microscope, separate for dentin and enamel margins.

Results: Over 90% of enamel margins exhibited no microleakage following cycling. Bleaching agents had almost no effect on numerical averages. Eighty-eight percent of the dentin margins were free of microleakage for the non-treated control group. Bleaching treatments collectively had slight numerical reductions to around 80%. The statistical evaluation (Kruskal-Wallis-test) showed no significant difference in microleakage between groups for enamel or dentin.

Conclusion: Bleaching with the materials tested had no influence on microleakage of Filtek Z250 composite bonded with Scotchbond 1.