Microwave irradiation has been used for disinfection of dentures instead of chemical solutions; yet, its effect on resin properties after repeated procedures still is unclear. This study evaluated the cumulative effect of two disinfection methods on Knoop microhardness and tridimensional stability of a poly(methyl methacrylate) denture base resin. For the microhardness measurement, 24-resin discs received mechanical polishing and were submitted to the following treatments: (1) control (no disinfection), (2) chemical disinfection (immersion in 100ppm chloride solution for 24h), or (3) microwave disinfection (irradiation at 690 W for 6 min). Disinfection procedures were performed twice (T1, T2) with a 7-day interval. Knoop microhardness was recorded after polishing (T0) and after T1 and T2. For the dimensional stability test (measured by the adaptation of the denture bases), 36-maxillary denture bases were obtained from type III dental stone casts duplicated from a metallic master model and submitted to the disinfection treatment. Adaptation of denture bases was measured at baseline (T0) and after T1 and T2 by weighing a vinyl polysiloxane film reproducing the gap between resin base and master model. Data were analyzed by ANOVA GLM for repeated measures and Bonferroni's test, alpha = 0.05. Knoop microhardness was not modified by any disinfection procedure but decreased over time. Denture resin bases submitted to microwave disinfection had gradual increase of distortion over time, while bases immersed in chloride solution did not differ from the control group and remained dimensionally stable from T1 to T2.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1002/jbm.b.31027 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Effect of In Situ Acid Erosion on Structural and Optical Properties of Nanoparticulated Bisacrylic Resin With Different Surface Treatments.
J Esthet Restor Dent
January 2025
Department of Dental Materials and Prosthodontics, Sao Paulo State University (UNESP), School of Dentistry, Araçatuba, São Paulo, Brazil.
Objective: To evaluate the influence of in situ acid erosion on the structural and optical properties of nanoparticulate bisacrylic resin with different surface treatments, evaluating surface roughness (Ra), knoop microhardness (KHN), color change (ΔE, ΔL, ΔC, ΔH), contrast (CR) and translucency (TP).
Methods: Eighty specimens were made (n = 10 per group) and the following surface treatments were applied: U-unpolished; A-polishing with Astropol rubber tips (Ivoclar); S-Biscover LV surface sealant (Bisco) and S-Palaseal surface sealant (kulzer). For the in situ experiment, 10 volunteers wore an intraoral appliance containing eight specimens (two specimens per experimental group), with only one specimen from each experimental group being subjected to the acid process.
Optical, Mechanical, and Chemical Impact of Brushing with Activated Charcoal Toothpowder and Toothpaste on Dental Enamel: An In Vitro Evaluation.
Materials (Basel)
December 2024
Department of Dentistry, Federal University of Maranhão (UFMA), São Luís 65080-805, MA, Brazil.
This in vitro study evaluated the effects of brushing with activated charcoal powder or toothpaste on enamel surface properties, including color change (ΔE), Knoop microhardness (HK), roughness (Ra), and the characteristics of the resulting brushing slurry [pH, fluoride (F), and calcium (Ca) concentration]. A total of 48 enamel samples were stained and divided into 4 groups ( = 12): activated charcoal toothpaste (AC-T), activated charcoal powder (AC-P), hydrogen peroxide-based whitening toothpaste (HP-T), and conventional toothpaste (C-T, positive control). The samples were subjected to a brushing cycling model, and ΔE, HK, Ra and enamel morphology were analyzed at baseline (T0) and after brushing cycle (T1).
View Article and Find Full Text PDFPrinted versus heat-polymerized resin for occlusal devices: Evaluation of physical and mechanical properties after brushing and microbial adhesion.
J Prosthodont
January 2025
Department of Dental Materials and Prosthesis, Ribeirão Preto Dental School, University of São Paulo (USP), Ribeirão Preto, Brazil.
Purpose: To evaluate the physical and mechanical properties after brushing and microbial adhesion of printed resins (PRs) and heat-polymerized resins (HRs) for occlusal devices (ODs).
Materials And Methods: Knoop microhardness and roughness were evaluated in three measurements before and after brushing with detergent or dentifrice. Flexural strength and modulus of elasticity were assessed by 3-point bending, and the adhesion of Candida albicans and Streptococcus mutans was evaluated by colony-forming units per milliliter (CFU/mL) and metabolic activity using the XTT assay only without brushing.
Remineralisation of enamel erosive lesions by daily-use fluoride treatments: network meta-analysis of an in situ study set.
Clin Oral Investig
December 2024
Oral Health Research Institute, Indiana University School of Dentistry, 415 Lansing Street, Indianapolis, IN, 46202-2876, USA.
Objectives: Daily-use fluoride products are first-line protection against enamel wear from dietary-acid exposure (DAE). This study aimed to understand effects of fluoride concentration, fluoride salt, product form and ingredients in daily-use products on remineralisation and demineralisation, via network meta-analysis (NMA) of 14 studies using one well-established in-situ model. Remineralisation (surface-microhardness recovery, SHMR) after treatment, and protection against subsequent demineralisation (acid-resistance ratio, ARR) were measured.
View Article and Find Full Text PDF3D-printed denture base resins: Glazing as an alternative to improve surface, mechanical, and microbiological properties.
J Prosthodont
December 2024
Department of Dentistry, Federal University of Rio Grande do Norte (UFRN), Natal, Rio Grande do Norte, Brazil.
Purpose: To evaluate the impact of glazing denture base resins (heat-polymerized and 3D-printed) on surface, mechanical, and microbiological properties.
Materials And Methods: Discs (10 × 3 mm) and bars (64 × 10 × 3.3 ± 0.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!