Objectives: The objective of this study was to investigate the use of benzoyl germanium derivatives as a novel visible light photoinitiator of resin-based dental composites. Selected mechanical properties, such as flexural strength and flexural modulus, setting time, storage stability, and UV light stability, of the composites based on the novel photoinitiators benzoyltrimethylgermane (BTMGe) or dibenzoyldiethylgermane (DBDEGe) were investigated and compared to the properties of materials that are cured with a mixture of camphorquinone (CQ) and ethyl 4-(N,N-dimethylamino)benzoate (EMBO).
Methods: The flexural strength and flexural modulus of elasticity were determined according to ISO 4049. For this purpose, test specimens (2 mm x 2 mm x 25 mm) of the composites investigated were prepared in stainless steel moulds and light-cured (150 mW/cm2, 2 s x 180 s). The flexural strength and flexural modulus of elasticity were measured after immersing the cured specimens in water for 24h at 37 degrees C and in certain cases, after they had been boiled for 24h in water. In addition, the setting time, curing depth, storage and UV stability of selected composites were determined.
Results: The novel photoinitiators BTMGe or DBDEGe can be used to substitute the binary photoinitiator CQ/EMBO in visible light-cured restorative composites. Especially, DBDEGe showed a significantly higher photocuring activity in composites with a filler load of about 60 wt. % in comparison to that of CQ/EMBO. In addition, composites based on BTMGe or DBDEGe showed an improved UV stability and a storage stability comparable to that of CQ/EMBO-based composites.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.dental.2007.11.004 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Enhanced mechanical properties and in vitro bioactivity of silicon nitride ceramics with SiO, YO, and AlO as sintering aids.
J Mech Behav Biomed Mater
January 2025
School of Materials Science and Engineering, University of Jinan, Jinan, 250022, China. Electronic address:
Silicon nitride (Si₃N₄) ceramics exhibit excellent mechanical properties and biocompatibility, making them highly suitable for biomedical applications, particularly in implants. In this study, the mechanical properties and bioactivity of Si₃N₄ ceramics with varying amounts of Y₂O₃-Al₂O₃-SiO₂ sintering aids were investigated. Increasing the sintering additive content from 4 wt% to 8 wt% substantially improved the bulk density of the ceramics, leading to notable enhancements in mechanical properties.
View Article and Find Full Text PDFFlexural Response Comparison of Nylon-Based 3D-Printed Glass Fiber Composites and Epoxy-Based Conventional Glass Fiber Composites in Cementitious and Polymer Concretes.
Polymers (Basel)
January 2025
School of Civil Engineering and Environmental Science, University of Oklahoma, 202 W Boyd St., Norman, OK 73019, USA.
With 3D printing technology, fiber-reinforced polymer composites can be printed with radical shapes and properties, resulting in varied mechanical performances. Their high strength, light weight, and corrosion resistance are already advantages that make them viable for physical civil infrastructure. It is important to understand these composites' behavior when used in concrete, as their association can impact debonding failures and overall structural performance.
View Article and Find Full Text PDFLignin Reinforcement in Polybutylene Succinate Copolymers.
Polymers (Basel)
January 2025
Department of Forest and Fire Sciences, University of Idaho, Moscow, ID 83844-1132, USA.
This study investigated the valorization of industrial lignin for producing biodegradable polybutylene succinate (PBS)-lignin copolymers. PBS was blended with varying lignin contents (0-45 wt. %) and crosslinked/grafted using dicumyl peroxide (DCP).
View Article and Find Full Text PDFThe Influence of Rice Husk Ash Incorporation on the Properties of Cement-Based Materials.
Materials (Basel)
January 2025
Green Environmental Protection Industry Co., Ltd., Guiyang 551109, China.
Rice husk ash is a kind of biomass material. Its main component is silicon dioxide, with a content of up to 80%. It has high pozzolanic activity and can react with hydroxide in cement.
View Article and Find Full Text PDFExperimental Study on Flexural Behaviour of Prefabricated Steel-Concrete Composite I-Beams Under Negative Bending Moment: Comparative Study.
Materials (Basel)
January 2025
School of Civil Engineering, Nanjing Tech University, Nanjing 211816, China.
The issues of numerous steel beam components and the tendency for deck cracking under negative bending moment zones have long been challenges faced by traditional composite I-beams with flat steel webs. This study introduces an optimized approach by modifying the structural design and material selection, specifically substituting flat steel webs with corrugated steel webs and using ultra-high-performance concrete for the deck in the negative bending moment zone. Three sets of model tests were conducted to compare and investigate the influence of deck material and web forms on the bending and crack resistance of steel-concrete composite I-beams under a negative bending moment zone.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!