Purpose: To measure the surface hardness and shear punch strength of six tooth-colored restorative materials before and after immersion in acidic and alkaline solutions.
Methods: Specimens were prepared from three resin composites; Ceram X, Filtek Supreme, Point 4, two polyacid-modified resin composites; Dyract, F2000, and one resin-modified glass-ionomer cement; Fuji II LC, immersed in distilled water for 24 hours at 60 degrees C, polished with silicon carbide papers up to 2000-grit and subjected to baseline measurement for Vickers hardness or shear punch strength. Further specimens were transferred to one of four aqueous media at 60 degrees C for a further 2 weeks; distilled water, 0.01 mol/L lactic acid, 0.1 N NaOH or coffee 15 g/500mL, washed, dried and tested for final hardness or shear punch strength.
Results: Data analysis using ANOVA and Tukey's test showed that the hardness and shear punch strength values were material and solution dependent. Regardless of the solutions; the hardness of F2000 was the highest and Fuji II LC the lowest; Point 4 and Filtek Supreme had the highest shear punch strength; Fuji II LC and F2000 had lowest. NaOH significantly reduced the hardness of all materials and completely dissolved the structure of Fuji II LC. Lactic acid and coffee significantly increased shear punch strength compared to baseline.
Download full-text PDF |
Source |
|---|
Publication Analysis
Top Keywords
Similar Publications
Influence of Structural Optimization on the Physical Properties of an Innovative FDM 3D Printed Thermal Barrier.
Materials (Basel)
December 2024
Department of Energy Conversion Engineering, Faculty of Mechanical and Power Engineering, Wroclaw University of Science and Technology, 27 Wybrzeze Wyspianskiego Street, 50-370 Wroclaw, Poland.
This article describes an innovative thermal insulation barrier in the form of a sandwich panel manufactured using 3D FDM printing technology. The internal structure (core structure) of the barrier is based on the Kelvin foam model. This paper presents the influence of the parameters (the height h and the porosity P of a single core cell) of the barrier on its properties (thermal conductivity, thermal resistance, compressive strength, and quasi-static indentation strength).
View Article and Find Full Text PDFEnhancing Meat Analog Texture Using Wet-Spun Fibroin Protein Fibers: A Novel Approach to Mimic Whole-Muscle Meat.
J Texture Stud
February 2025
Institute for Advanced Biosciences, Keio University, Tsuruoka, Japan.
The increasing demand for protein-rich, plant-based foods has driven the development of meat analogs that closely mimic the texture and mouthfeel of animal meat. While plant-based fibrils and electrospun silk fibroin fibers have been explored for texture enhancement and scaffolding in both meat analogs and cell-based meats, the use of wet-spun fibroin protein fibers as a food ingredient remains underexplored. This study investigates the potential of wet-spun recombinant fibroin fibers to enhance the textural properties of meat analogs.
View Article and Find Full Text PDFExplainable prediction model for punching shear strength of FRP-RC slabs based on kernel density estimation and XGBoost.
Sci Rep
December 2024
Department of Civil and Architectural Engineering, University of Miami, Coral Gables, FL, 33146, USA.
Reinforced concrete (RC) slabs are widely used in modern building structures due to their superior properties and ease of construction. However, their mechanical properties are limited by their punching shear strength in the connection region with the columns. Researchers have attempted to add steel reinforcement in the form of studs and randomly distributed fibers to concrete slabs to improve the punching strength.
View Article and Find Full Text PDFThe Impact of Reinforcement Ratio on the Punching Shear of CFRP Grid-Reinforced Concrete Two-Way Slabs.
Materials (Basel)
November 2024
Civil Engineering School, Southeast University, Nanjing 211102, China.
Corrosion of steel reinforcement in concrete slabs undermines structural durability and shortens the lifespan of concrete structures. Carbon Fiber-Reinforced Polymer (CFRP) is a promising material offering benefits such as high strength, corrosion resistance, and light weight. This study aims to investigate the punching shear performance of concrete slabs reinforced with CFRP grids, focusing on the effects of different reinforcement ratios.
View Article and Find Full Text PDFMicrostructure and Microhardness Evolution of Mg-8Al-1Zn Magnesium Alloy Processed by Differential Speed Rolling at Elevated Temperatures.
Materials (Basel)
August 2024
Department of Manufacturing Engineering Technology, College of Technological Studies, The Public Authority of Applied Education and Training (PAAET), P.O. Box 42325, Shuwaikh 70654, Kuwait.
Mg-8Al-1Zn magnesium alloy was successfully processed using deferential speed rolling (DSR) at temperatures of 400 and 450 °C for thickness reduction of 30, 50, and 70% with no significant grain growth and dynamic recrystallization. Using optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM), the rolled microstructures were examined. Although the results indicate a slight reduction in grain size from the initial condition, the DSR processing of alloy at an elevated temperature was associated with a significant number of twins and a distribution of the fine particles of the second phase.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!