Unlabelled: The aim of the study was to asses the influence of the time, method and type of light curing on the compressive strength of dental composites. Dental composite resin (T-Econom, Ivoclar Vivadent) was cured for 10, 30 or 40 sec. with either a commercial conventional halogen light curing unit (LCU)--Hilux, (Benliodlu Dental Inc), or a light emitting diode (LED), LCU-Bluedent LED Smart. The compressive strengths were determined after 72 h on samples 3 mm in diameter and 7 mm high using FPZ 100/1 device.
Results: The samples cured with LED LCU for 40 seconds in pulse mode showed the smallest values of compressive strength (245 MPa), while those cured with LED LCU for 40 seconds in ramp mode reached the highest values (295 MPa). Similar values for compressive strength were found for the samples polymerized with conventional halogen LCU and the samples cured with LED LCU in constant mode (283 MPa and 285 MPa, respectively).
Conclusions: Compressive strength depends on the light type and method. Tested LED curing light seems to induce similar compressive strengths as the halogen-based light. Using this conventional light curing unit requires at least 40 seconds of exposure in order to achieve adequate compressive strength. The LED light curing unit should be used in the ramp mode for at least 40 sec, followed by 10 sec in fast mode in order to achieve the best results.
Download full-text PDF |
Source |
|---|
Publication Analysis
Top Keywords
Similar Publications
Mechanical and microstructural properties of fiber-reinforced basalt rock cutting waste-based geopolymer composites exposed to high temperatures.
Environ Sci Pollut Res Int
January 2025
Institute of Science, Nevşehir Hacı Bektaş Veli University, Nevşehir, Türkiye.
Managing basalt rock cutting waste in an environmentally responsible manner is crucial to mitigate its negative impacts and protect both the environment and human health. Recycling basalt rock cutting waste in geopolymer applications offers multiple environmental, economic, and performance benefits, making it a promising approach for sustainable construction practices. For this purpose, this study concerns about the performance of fiber-reinforced basalt rock-cutting waste-based geopolymer composites at high temperatures up to 1000 °C.
View Article and Find Full Text PDFExperimental and analytical study on axial behaviour of square corrugated concrete filled single and double skin tube stub columns.
Sci Rep
January 2025
Department of Structural Engineering, Faculty of Engineering, Mansoura University, Mansoura, Egypt.
Concrete-filled double-skin steel tubular (CFDST) columns have become widely utilized in building construction and bridges, thanks to their exceptional structural capabilities. Therefore, this study investigates the axial compressive behavior of square CFDST columns. The study aims to explore the influence of external and internal plate shapes (flat or corrugated plates) and different widths of internal steel tubes on the axial compressive behavior.
View Article and Find Full Text PDFEngineering geological evaluation of Bowa Dayole dam site, North Shewa Zone, Oromia, Ethiopia.
Heliyon
January 2025
Department of Mining Engineering, College of Engineering, Addis Ababa Science and Technology University, Addis Ababa, P.O. Box: 16417, Ethiopia.
Developing nations like Ethiopia face food and water shortages due to weather and droughts. The Bowa Dayole masonry gravity dam is expected to irrigate farmland downstream. Despite this, the engineering geology is complicated by the presence of highly fractured and weathered aphanitic basaltic rock, along with a weak unwelded to welded tuff rock mass in the dam foundation.
View Article and Find Full Text PDFFabrication and characterization of 3D-printed polymeric-based scaffold coated with bioceramic and naringin for a potential use in dental pulp regeneration (in vitro study).
Int Endod J
January 2025
Restorative and Aesthetic Dentistry Department, College of Dentistry, University of Baghdad, Baghdad, Iraq.
Aim: 3D-printed scaffolds loaded with healing directed agents could be employed for better treatment outcome in regenerative dentistry. The aim of this study was to fabricate and characterize simple 3D-printed poly lactic acid (PLA) scaffolds coated with nanoHydroxyapatite (nHA), Naringin (NAR), or their combination, and testing their morphological, chemical, mechanical, antibacterial, biocompatible and bioactive properties.
Methodology: Two variants pore sizes, 300 and 700 μm, of 3D-printed PLA disc scaffolds measuring (10 × 1 mm) were fabricated.
Collagen Nanofiber-Lignin Composite Sponges with Adjustable Hierarchical Pore Structure for Efficient Low-Frequency Sound Absorption.
Adv Sci (Weinh)
January 2025
Department of Biotechnology, College of Life Science and Technology, Huazhong University of Science and Technology, Wuhan, 430074, China.
Current sound-absorbing materials, reliant on nonrenewable resources, pose sustainability and disposal challenges. This study introduces a novel collagen-lignin sponge (CLS), a renewable biomass-based material that combines collagen's acoustic properties with lignin's structural benefits. CLSs demonstrate high porosity (>0.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!