Aim: To compare the shear bond strength of a nano-hybrid restorative material, Grandio (Voco, Cuxhaven, Germany), to that of a traditional adhesive material (Transbond XT; 3M Unitek, Monrovia, CA, USA) when bonding orthodontic brackets.
Material And Methods: Forty teeth were randomly divided into 2 groups: 20 teeth were bonded with the Transbond adhesive system and the other 20 teeth with the Grandio restorative system, following manufacturer's instructions. Student t test was used to compare the shear bond strength of the 2 systems. Significance was predetermined at P 5 .05.
Results: The t test comparisons (t = 0.55) of the shear bond strength between the 2 adhesives indicated the absence of a significant (P = .585) difference. The mean shear bond strength for Grandio was 4.1 +/- 2.6 MPa and that for Transbond XT was 4.6 +/- 3.2 MPa. During debonding, 3 of 20 brackets (15%) bonded with Grandio failed without registering any force on the Zwick recording. None of the brackets bonded with Transbond XT had a similar failure mode.
Conclusions: The newly introduced nano-filled composite materials can potentially be used to bond orthodontic brackets to teeth if its consistency can be more flowable to readily adhere to the bracket base.
Download full-text PDF |
Source |
|---|
Publication Analysis
Top Keywords
Similar Publications
Evaluation of the Effect of Chitosan-Based Irrigation Solutions on the Bond Strength of Mineral Trioxide Aggregate to Bulk-Fill Composite.
J Funct Biomater
December 2024
Department of Endodontics, Faculty of Dentistry, Gazi University, 06490 Ankara, Türkiye.
Bond strength between repair and restorative materials is crucial for endodontic success. This study assessed the effects of the following final irrigation solutions on the bond strength of mineral trioxide aggregate (MTA) to a bulk-fill composite: (1) 17% Ethylenediamine tetraacetic acid (EDTA); (2) 2% Chlorhexidine (CHX); (3) 0.2% chitosan; (4) 0.
View Article and Find Full Text PDFEffect of Mechanical Surface Treatment on Shear Bond Strength of Orthodontic Brackets to 3D Printed and Milled CAD/CAM Provisional Materials: An In Vitro Study.
J Funct Biomater
November 2024
King Abdullah International Medical Research Center, Riyadh 11481, Saudi Arabia.
The aim of the study is to assess the impact of mechanical surface treatments on the shear bond strength (SBS) of orthodontic brackets bonded to three-dimensional (3D) printed and milled CAD/CAM provisional materials. Sixty cylindrical samples were fabricated for each provisional material. Samples were treated with one of the following surface treatments: aluminum oxide airborne particle abrasion, diamond bur rotary instrument roughening, and phosphoric acid etching (control).
View Article and Find Full Text PDFEvaluation of Shear Bond Strength of Lithium Disilicate Veneers Using Pre-heated Resin Composite With Two Conventional Resin Cements: An In Vitro Study.
Cureus
November 2024
Department of Endodontic and Operative Dentistry, Damascus University, Damascus, SYR.
Objectives This study aimed to compare the shear bond strength of three resin cements (light-cured resin cement, pre-heated composite resin, and dual-cured self-adhesive resin cement) when bonding to lithium disilicate discs. Materials and methods Thirty-six discs made of lithium disilicate were fabricated and etched with 9.5% (HF), and 36 human premolars were collected and immersed in the acrylic molds, then randomly divided into three equal groups (n = 12): Group 1: light-cured resin cement, Group 2: pre-heated resin composite, and Group 3: dual-cured resin cement.
View Article and Find Full Text PDFEvaluation of the shear bond strength of surface-treated Cobalt-Chromium metal crowns on corticobasal® implant abutments cemented using different luting agents.
J Stomatol Oral Maxillofac Surg
December 2024
Reader, Department of Periodontics, Saveetha Dental College and Hospitals, Saveetha Institute of Medical and Technical Sciences, Saveetha University, Chennai 600077, Tamil Nadu, India.. Electronic address:
Purpose: This in-vitro study aimed to compare the shear bond strength (SBS) of cobalt-chromium (Co-Cr) crowns on Corticobasal® implant abutments, evaluating the effects of two surface treatments and two luting agents.
Materials And Methods: Thirty Co-Cr crowns were fabricated using CAD-CAM technology with a direct metal laser sintering process and divided into three groups based on surface treatment: Group I (untreated), Group II (sandblasted with 50 μm Al₂O₃), and Group III (Er: YAG laser etching). Each group was further subdivided based on luting cement: Sub group A (GC Fuji Plus) and Sub group B (Rely X U200).
An Survey on the Effect of Six Commercial Brands of Phosphoric Acid on the Micro-shear Bond Strength of Composite Resin to Enamel.
J Dent (Shiraz)
December 2024
Dept. of Restorative Dentistry, Dental Research Center, School of Dentistry, Birjand University of Medical Sciences, Birjand, Iran.
Statement Of The Problem: One of the most important factors in the clinical longevity of composite resin restorations is proper adhesion, which is achieved using phosphoric acid. Different phosphoric acid products might affect the micro-shear bond strength of composite resin to enamel.
Purpose: The present study aimed to evaluate the micro-shear bond strength of composite resin to sound enamel using six different brands of acid-etch agents.