Purpose: To investigate the influence of the acid-base reaction between acidic monomers and amines on the polymerization behavior of self-etching, self-curing adhesives, determine the effect of the application mode on the shear bond strength and morphology, and elucidate the adhesion performance of such systems by shear bond strength measurements.
Materials And Methods: The amine redox-initiator system N,N-di(2-hydroxyethyl)p-toluene (DEPT)/dibenzoyl peroxide (BPO) was selected to investigate the influence of the amine-base reaction on polymerization behavior. The PKa value of DEPT hydrochloride was measured by titration with NaOH. The influence of the pH value and DEPT concentration on the polymerization rate of methacrylates was investigated by exotherm time measurements. Three different application protocols of Multilink Primer (Ivoclar Vivadent) and Panavia 21 ED-Primer (Kuraray) were tested, 15 s passive vs 15 s agitation vs 60 s passive in combination with the corresponding resin luting material. The effects of these three application protocols were evaluated and monitored by both shear bond strength tests and SEM characterization of the surface morphology. The adhesion potential of these self-etching, self-curing luting systems was compared on enamel and dentin both directly after application and after 24 h.
Results: The pKa of DEPT-HCl is 4.45. The polymerization rate of the DEPT-containing, self-etching, self-curing adhesive system is highly influenced by both the amine concentration and the pH value. In the case of Multilink, agitation of the primer mixture for 15 s, especially on dentin, resulted in a higher bond strength and a more pronounced removal of the smear layer. Multilink resulted in statistically higher bond strengths (p < 0.05) than Panavia 21 for both the enamel and dentin directly after application and for the dentin after 24 h.
Conclusion: Radical polymerization initiators used in self-curing systems are strongly adversely affected by acidic monomers incorporated in self-etching adhesives. However, if there is a good adjustment of these components and effects of adhesive application are taken in account, high bond strengths can be achieved.
Download full-text PDF |
Source |
|---|
Publication Analysis
Top Keywords
Similar Publications
Flexural Response Comparison of Nylon-Based 3D-Printed Glass Fiber Composites and Epoxy-Based Conventional Glass Fiber Composites in Cementitious and Polymer Concretes.
Polymers (Basel)
January 2025
School of Civil Engineering and Environmental Science, University of Oklahoma, 202 W Boyd St., Norman, OK 73019, USA.
With 3D printing technology, fiber-reinforced polymer composites can be printed with radical shapes and properties, resulting in varied mechanical performances. Their high strength, light weight, and corrosion resistance are already advantages that make them viable for physical civil infrastructure. It is important to understand these composites' behavior when used in concrete, as their association can impact debonding failures and overall structural performance.
View Article and Find Full Text PDFMechanical Properties and Decomposition Behavior of Compression Moldable Poly(Malic Acid)/-Tricalcium Phosphate Hybrid Materials.
Polymers (Basel)
January 2025
Department of Materials and Applied Chemistry, College of Science and Technology, Nihon University, 1-8-14 Kandasurugadai, Chiyoda-ku, Tokyo 101-8308, Japan.
Calcified tissues in living organisms, such as bone, dentin, and enamel, often require surgical intervention for treatment. However, advances in regenerative medicine have increased the demand for materials to assist in regenerating these tissues. Among the various forms of calcium phosphate (CaP), tricalcium phosphate (TCP)-particularly its α-TCP form-stands out due to its high solubility and efficient calcium release, making it a promising candidate for bone regeneration applications.
View Article and Find Full Text PDFRecent Advances in Paper Conservation Using Nanocellulose and Its Composites.
Molecules
January 2025
Institute for Preservation and Conservation of Chinese Ancient Books, Fudan University Library, Fudan University, 220 Handan Road, Shanghai 200433, China.
Paper-based cultural relics experience aging and deterioration during their long-term preservation, which poses a serious threat to their lifetime. The development of conservation materials with high compatibility and low intervention has been expected to extend the lifetime of paper artifacts. As a new type of biological macromolecule, nanocellulose has been extensively utilized in paper conservation, attributed to its excellent paper compatibility, high optical transparency, outstanding mechanical strength, and large specific surface area with abundant hydroxyl groups.
View Article and Find Full Text PDFA Study on the Impact of Temperature on the Anchoring Durability of Carbon-Fiber-Reinforced Polymer Cables.
Materials (Basel)
January 2025
School of Civil & Environmental Engineering and Geography Science, Ningbo University, Ningbo 315211, China.
To improve the application of carbon-fiber-reinforced polymers (CFRPs) in civil engineering, the long-term durability of CFRP anchorage systems has become a critical issue. Temperature fluctuations can significantly impact the bond performance between CFRPs and the load transfer medium (LTM), making it essential to understand the effects of temperature on the durability of CFRP anchorages. Therefore, this study investigates the influence of temperature on the durability of CFRP anchorages through aging tests on 30 epoxy-filled CFRP-bonded anchorage specimens, followed by pull-out tests.
View Article and Find Full Text PDFA Study on the Effect of Nickel-Plated Graphite Content on the Microstructure and Properties of AlZn/Nickel-Plated Graphite Composite Cold Spray Coatings.
Materials (Basel)
January 2025
School of Physical and Technology, Wuhan University, Wuhan 430072, China.
Aluminum and its alloys are widely used in the busbar structures of electrolytic aluminum production. However, they are prone to corrosion and wear damage during use, leading to a decline in current-transmission efficiency and potentially causing safety issues. To repair damaged aluminum busbars, this paper explores the feasibility of using cold spraying technology for surface restoration.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!