Synthesis and luminescence of zinc and europium alpha-thiophene carboxylate polymer.

The zinc and europium alpha-thiophene carboxylate polymer with very strong red luminescence was prepared by rheological phase reaction method from zinc acetate, europium oxide and alpha-thiophenecarboxylic acid. Molecular weight, thermal analyses and X-ray diffraction pattern were measured. 1H NMR, 13C NMR, IR, XPS, UV, excitation and emission spectra were studied. The polymer with amorphous structure and 7.565x10(5) g/mol weight-average molecular exhibited excellent solubility in common organic solvents and better thermal stability under 270 degrees C in air. The quantum yield of the polymer in acetone was 0.6 relative to quinoline in 0.05 mol/l H(2)SO(4) solution. The energy of the pi,pi(*) excited state of C(4)H(3)SCO(2)(-) can be transferred to Eu(3+) ion resulting in emission from the 5D(0)-->(7)F(j) of Eu(3+) ion through the polymeric chains. Zn(2+) can effectively enhance the luminescence of Eu(3+) in alpha-thiophenecarboxylate polymer.