A comparative study on compositional changes and Knoop hardness measurement of the cavity floor prepared by Er:YAG laser irradiation and mechanical bur cavity.

Objective: This present study was performed to compare the compositional changes of human dentin and, Knoop hardness of the cavity floor prepared by Er:YAG laser irradiation with that of the conventional bur cavity.

Background Data: There are still no reports on the compositional changes of dental hard tissues and microhardness of the cavity floor prepared by Er:YAG laser irradiation.

Materials And Methods: Fifteen laser and 15 bur cavities were cross-sectioned, and subjected to atomic analysis by SEM-EDX and Knoop hardness testing. Statistical analyses were performed using the Mann-Whitney U test; a value of p < 0.01 was considered significant. Cross sections of the remaining five laser and five bur cavities were examined by light microscopy and then by SEM.

Results: The results showed that the quantities of Ca (Ca weight %) and P (P weight %) were increased significantly in the laser cavities, but no significant differences were found between the Ca/P ratio and Knoop hardness number of laser and bur cavities. The results of SEM observation revealed that the lased cavity surface was irregular, and there was also the absence of a smear layer; the orifice of dentinal tubules was exposed.

Conclusion: Er:YAG laser device produces minimal thermal induced changes of dental hard tissue compositions; Ca/P ratio and Knoop hardness of the lased cavity floor was almost similar to the bur cavities.