Formation of a bioconjugate composed of hemin, smectite, and quaternary ammonium chloride that is soluble and active in hydrophobic media.

Hemin (Fe(3+)) was adsorbed onto synthetic smectite (clay mineral) intercalated with a quaternary alkenylammonium compound, dioleyldimethylammonium chloride (DOA), to form a hemin-smectite-DOA conjugate. The hemin-smectite-DOA conjugate was soluble in organic solvents such as benzene and toluene to form a transparent colloidal solution with a light yellow color. Its absorption spectrum in benzene showed two bands, 600 and 568 nm, in the visible region and a sharp Soret band at 400 nm with the molar extinction coefficient of 7.5 x 10(4) M(-1) cm(-1). The formation of the conjugate of smectite and DOA was confirmed by X-ray diffraction analysis: the basal spacing, d(001), of hemin-smectite-DOA conjugate was 19 A which is an expansion of the interlayer space by 5 A based upon the basal spacing of smectite of 14 A. Hemin-smectite-DOA conjugate catalyzed the peroxidase-like reaction in organic solvents using benzoyl peroxide as the hydrogen acceptor and leucocrystal violet as the hydrogen donor. The temperature-dependent peroxidase-like activity of the conjugate was compared with peroxidase activity of horseradish peroxidase. The hemin-smectite-DOA conjugate exhibited higher activity as the temperature was increased from 30 to 70 degrees C, while horseradish peroxidase activity was reduced as the temperature was increased.