Purpose: To determine and compare the localized wear of six compomer restorative materials.
Materials And Methods: Ten specimens of Dyract, Dyract AP, F2000, Compoglass F, Elan and Hytac were prepared in a custom fixture and polished. A pretest surface profile was generated using an MTS 3-D surface profilometer and the specimens were subjected to 400,000 cycles in a Leinfelder wear machine equipped with a conical stylus tip to simulate localized wear. A post-test profile was generated and the before and after profiles were fitted and analyzed using AnSur 3-D software. The total volume loss and depth of the wear facet on each specimen was calculated and statistical analysis was accomplished (ANOVA and Tukey's test).
Results: Volume loss (mm3) was as follows: F2000, 0.027 +/- 0.002; Hytac, 0.007 +/- 0.023; Elan, 0.054 +/- 0.013; Compoglass F, 0.135 +/- 0.006; Dyract AP, 0.135 +/- 0.023; Dyract, 0.185 +/- 0.032. Maximum depth of the wear facets (microm) was as follows: F2000, 112.2 +/- 10.2; Hytac, 132.8 +/- 9.3; Elan, 144.3 +/- 23. 1; Compoglass F, 168.3 +/- 13.0; Dyract AP, 194.0 +/- 19.7; Dyract, 220.6 +/- 15.8. There was not a difference (P > 0.05) in volumetric loss between F2000 and Hytac or between Hytac and Elan. The volume loss and maximum depth of the wear facets of F2000, Hytac and Elan was significantly less (P< 0.05) than Compoglass F, Dyract AP and Dyract The results of this study indicate that there are significant differences in the in vitro wear rates of compomer materials.
Download full-text PDF |
Source |
|---|
Publication Analysis
Top Keywords
Similar Publications
Mechanical Considerations and Clinical Implications of Joint Arthroplasty Metallosis.
Cureus
December 2024
Orthopedic Surgery, Middlebrook Family Medicine, Middlebrook, USA.
The treatment for osteoarthritis (OA) often requires total joint arthroplasty (TJA) when less invasive approaches fail. The annual incidence of TJA is rising. Metal-on-metal (MoM) hip and knee implants were widely used for TJA in the past, but complications have led to their decline.
View Article and Find Full Text PDFGeochemical signatures and nanomechanical properties of echinoid tests from nearshore habitats of Florida: environmental and physiological controls on echinoid biomineralization.
PeerJ
January 2025
Florida Museum of Natural History, University of Florida, Gainesville, FL, United States of America.
The mechanisms that regulate minor and trace element biomineralization in the echinoid skeleton can be primarily controlled biologically (, by the organism and its vital effects) or by extrinsic environmental factors. Assessing the relative role of those controls is essential for understanding echinoid biomineralization, taphonomy, diagenesis, and their potential as geochemical archives. In this study, we (1) contrast geochemical signatures of specimens collected across multiple taxa and environmental settings to assess the effects of environmental and physiological factors on skeletal biomineralogy; and (2) analyze the nanomechanical properties of the echinoid skeleton to assess potential linkages between magnesium/calcium (Mg/Ca) ratios and skeletal nanohardness.
View Article and Find Full Text PDFImplantation of Heparin-Conjugated Fibrin Hydrogel for Local Defects of Cartilage in Knee Osteoarthritis: A Case Report.
Int Med Case Rep J
January 2025
National Scientific Center of Traumatology and Orthopedics Named After Academician Batpenov N.D., Astana, Kazakhstan.
Background: Cartilage defects in the knee joint are areas of damage and wear to the cartilage that normally covers and protects the ends of bones. These defects occur due to sudden injuries, such as trauma or sports accidents, or due to chronic conditions, such as osteoarthritis. Cartilage acts as a shock absorber (cushion absorber), reducing the impact of mechanical stress on the joints, which helps prevent bone damage during movement.
View Article and Find Full Text PDFTherapeutic Potential of Targeting Ferroptosis in Periprosthetic Osteolysis Induced by Ultra-High-Molecular-Weight Polyethylene Wear Debris.
Biomedicines
January 2025
Department of Orthopedic Surgery, Faculty of Medicine, Graduate School of Medicine, Hokkaido University, Kita-15, Nish-7, Kita-ku, Sapporo 060-8638, Japan.
Periprosthetic osteolysis is the primary cause of arthroplasty failure in the majority of patients. Mechanistically, wear debris released from the articulating surfaces of a prosthesis initiates local inflammation and several modes of regulated cell death programs, such as ferroptosis, which represents a promising therapeutic target in various chronic inflammatory diseases. Thus, the current study aimed at exploring the therapeutic potential of targeting ferroptosis in a polyethylene-wear-debris-induced osteolysis model.
View Article and Find Full Text PDFGlenoid wear and migration pattern of a humeral head resurfacing implant: a prospective study using radio stereometric analysis.
JSES Int
November 2024
Department of Clinical Sciences at Danderyd Hospital, Karolinska Institutet, Stockholm, Sweden.
Background: The humeral head resurfacing arthroplasty (HHR) is normally used as a hemi shoulder arthroplasty and has been in use for the treatment of Gleno-Humeral osteoarthritis (OA) of the shoulder for more than 30 years. Some studies, however, shows that anatomical total shoulder arthroplasty provides better improvement in function than a HHR for patients with OA. Reasons for this may be a progressive glenoid wear (GW) or loosening of the HHR.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!