Objectives: Micromechanical retention from the hybrid layer is generally believed to be the mechanism of adhesion of current generation dentin bonding agents. The purpose of this investigation is to evaluate the interfacial fracture toughness of a commercial dentin bonding agent with and without this hybrid layer.
Methods: Ten extracted molars (AB2) were flattened on the occlusal surface, All-Bond 2 Universal Adhesive System (Bisco) was applied according to manufacturer's directions and a resin composite (Prodigy, Kerr) crown was formed. Another group of ten molars (AB2Cl) was handled identically with the exception of a 1 min gentle scrubbing application of 5.25% sodium hypochlorite after acid etching to remove the acid-exposed collagen. Plane-strain chevron-notch short bar fracture toughness specimens were fabricated from all 20 composite crowns and tested according to ASTM E1304-89. Each group was tested to failure in tensile mode at 0.1 mm min-1 and the maximum load at failure was used to determine plane-strain fracture toughness (KQvM). Weibull parameters were calculated and fracture probability distributions were tested for significant difference at the 95% confidence level. Scanning electron microscopy was employed on broken specimens (18/20) to describe the failure mode.
Results: Weibull distributions were not significantly different with characteristic plane-strain fracture toughness from maximum load (KQvM0) of 0.97 MPa m1/2 and 0.81 MPa m1/2 and a Weibull modulus of 4.7 and 3.9, respectively, for AB2 and AB2Cl. All AB2 samples failed within the adhesive joint, while the AB2Cl crack propagated from the interphase of adhesive resin and dentin to 1-2 microns into dentin.
Significance: Under the conditions of this study, the presence of collagen did not contribute to a significantly stronger bonded joint. Interfacial fracture toughness evaluation of the dentin-resin composite bimaterial interface shows promise for future investigations.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/s0109-5641(98)00014-1 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
The effect of SiC and YO inclusion on microstructure and mechanical properties of Al 5052 composite fabricated through Friction Stir Process.
Heliyon
January 2025
AU-Sophisticated Testing and Instrumentation Centre (AU-STIC), CoE-Advanced Materials Synthesis (CoE-AMS), Department of Mechanical Engineering, Alliance School of Applied Engineering, Alliance University, Bengaluru, 562106, India.
A consistent research attempt to develop newer lightweight-high strength materials facilitates the automobile sector to excel in product efficiency. The present research is another endeavour to anchor the automobile industries by exploring novel composite. The different earth elements SiC and YO are utilised for the hybrid reinforcement of Al 5052 alloy in four different weight proportions.
View Article and Find Full Text PDFDeveloping tough, fatigue-resistant and conductive hydrogels growth of metal dendrites.
Mater Horiz
January 2025
College of Materials Science & Engineering, Zhejiang University of Technology, Hangzhou 310014, P. R. China.
Developing hydrogels with high conductivity and toughness a facile strategy is important yet challenging. Herein, we proposed a new strategy to develop conductive hydrogels by growing metal dendrites. Water-soluble Sn ions were soaked into the gel and then converted to Sn dendrites an electrochemical reaction; the excessive Sn ions were finally removed by water dialysis, accompanied by dramatic shrinkage of the gel.
View Article and Find Full Text PDF3D nanocomposites of β-TCP-HBO-Cu with improved mechanical and biological performances for bone regeneration applications.
Sci Rep
January 2025
Advanced Glass and Glass Ceramic Research Laboratory, Department of Physics, University of Lucknow, Lucknow, 226007, India.
Recently, 3-D porous architecture of the composites play a key role in cell proliferation, bone regeneration, and anticancer activities. The osteoinductive and osteoconductive properties of β-TCP allow for the complete repair of numerous bone defects. Herein, β-TCP was synthesized by wet chemical precipitation route, and their 3-D porous composites with HBO and Cu nanoparticles were prepared by the solid-state reaction method with improved mechanical and biological performances.
View Article and Find Full Text PDFEnhanced mechanical properties and in vitro bioactivity of silicon nitride ceramics with SiO, YO, and AlO as sintering aids.
J Mech Behav Biomed Mater
January 2025
School of Materials Science and Engineering, University of Jinan, Jinan, 250022, China. Electronic address:
Silicon nitride (Si₃N₄) ceramics exhibit excellent mechanical properties and biocompatibility, making them highly suitable for biomedical applications, particularly in implants. In this study, the mechanical properties and bioactivity of Si₃N₄ ceramics with varying amounts of Y₂O₃-Al₂O₃-SiO₂ sintering aids were investigated. Increasing the sintering additive content from 4 wt% to 8 wt% substantially improved the bulk density of the ceramics, leading to notable enhancements in mechanical properties.
View Article and Find Full Text PDFFracture Toughness of Winding Carbon Plastics Based on Epoxy Matrices and Reinforced by Polysulfone Film.
Polymers (Basel)
January 2025
N.N. Semenov Federal Research Center for Chemical Physics, Russian Academy of Sciences, 119991 Moscow, Russia.
In this work, the fracture mechanism of winding carbon-fiber-reinforced plastics (CFRPs) based on epoxy matrices reinforced by polysulfone film was investigated. Two types of polymer matrices were used: epoxy oligomer (EO) cured by iso-methyltetrahydrophthalic anhydride (iso-MTHPA), and EO-modified polysulfone (PSU) with active diluent furfuryl glycidyl ether (FGE) cured by iso-MTHPA. At the winding stage, the reinforcing film was placed in the middle layer of the CFRP.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!