Fatigue behavior of freestanding nickel-molybdenum-tungsten thin films with high-density planar faults.

This research addresses the fatigue behavior of freestanding nickel-molybdenum-tungsten (Ni-Mo-W) thin films with high-density planar faults. The as-deposited Ni-Mo-W thin films demonstrate an unprecedented fatigue life, withstanding over a million cycles at a Goodman stress amplitude () of 2190 MPa - nearly 80% of the tensile strength. The texture, columnar grain width, planar fault configuration (spacing and orientation), and tensile strength were unchanged after annealing at 500 °C for 24 hours, and the film endured over 2 × 10 cycles at of 1050 MPa.