Microwave synthesis of zinc sulfite and porous zinc oxide microrods.

ZnSO(3) microrods with uniform size and shape can be prepared under microwave irradiation at much higher speed than a conventional heating bath, usually in minutes. The annealing of ZnSO(3) microrods produced porous ZnO microrods with pore size between 50-200 nm.

Towards aqueous gold nanoparticles with buffer resistance and high concentration.

High-concentration gold nanoparticles stabilized by poly(vinylpyrrolindone) (PVP) are prepared through modified citrate-reduction method. The modified approach possesses all the advantages of the popular citrate reduction method. With PVP as weak ligands as well as spatial effects for the metal nanoparticles, the control of the size and size distribution of the gold nanoparticles in the size range between 10 and 30 nm was achieved via maintaining balanced nucleation and growth by tuning the feed ratios of the metal precursors and reducing reagents.

Green chemistry for large-scale synthesis of semiconductor quantum dots.

Large-scale synthesis of semiconductor nanocrystals or quantum dots (QDs) with high concentration and high yield through simultaneously increasing the precursor concentration was introduced. This synthetic route conducted in diesel has produced gram-scale CdSe semiconductor quantum dots (In optimal scale-up synthetic condition, the one-pot yield of QDs is up to 9.6g).