Homo-Site Nucleation Growth of Twisted Bilayer MoS with Commensurate Angles.

Moiré superlattices, composed of two layers of transition metal dichalcogenides with a relative twist angle, provide a novel platform for exploring the correlated electronic phases and excitonic physics. Here, a gas-flow perturbation chemical vapor deposition (CVD) approach is demonstrated to directly grow MoS bilayer with versatile twist angles. It is found that the formation of twisted bilayer MoS homostructures sensitively depends on the gas-flow perturbation modes, correspondingly featuring the nucleation sites of the second layer at the same (homo-site) as or at the different (hetero-site) from that of the first layer.

Metal-organic complex coating for enhanced corrosion control and biocompatibility on biodegradable magnesium alloy for orthopaedic implants.

Magnesium alloy is currently regarded as the most favourable biodegradable metal; however, obstacles remain to be overcome in terms of managing its corrosion and ensuring its biocompatibility. In this study, a metal-organic complex comprising Ca ions incorporated in tannic acid (TA) was prepared and used to coat magnesium alloy by chemical conversion and dipping processes, followed by modification with stearic acid (SA). This metal-organic complex coating was demonstrated to be homogeneous and compact, and it significantly improved the electrochemical corrosion resistance and long-term degradation behaviour of the coated samples.

A "built-up" composite film with synergistic functionalities on Mg-2Zn-1Mn bioresorbable stents improves corrosion control effects and biocompatibility.

Control of premature corrosion of magnesium (Mg) alloy bioresorbable stents (BRS) is frequently achieved by the addition of rare earth elements. However, limited long-term experience with these elements causes concerns for clinical application and alternative methods of corrosion control are sought after. Herein, we report a "built-up" composite film consisting of a bottom layer of MgF conversion coating, a sandwich layer of a poly (1, 3-trimethylene carbonate) (PTMC) and 3-aminopropyl triethoxysilane (APTES) co-spray coating (PA) and on top a layer of poly (lactic-co-glycolic acid) (PLGA) ultrasonic spray coating to decorate the rare earth element-free Mg-2Zn-1Mn (ZM21) BRS for tailoring both corrosion resistance and biological functions.

One-Pot but Two-Step Vapor-Based Amine- and Fluorine-Bearing Dual-Layer Coating for Improving Anticorrosion and Biocompatibility of Magnesium Alloy.

Hydrophobic coating is of great interest to enhance the corrosion resistance of magnesium alloy implants, which always suffer from rapid corrosion that leads to the failing application under physiological conditions. Plasma-polymerized fluorocarbon (C-F) coating has been widely studied as a substrate protection layer; however, the precise control of the deposition rate of C-F coating with fluorinated alkanes has been a challenge. In this study, a thin, uniform, pinhole-free, polymerlike, and hydrophobic C-F coating was successfully prepared using acetylene (CH) as a cross-linking agent, which endows the coating with tunable properties of deposition rate by incorporation of unsaturated bonds.