[Synthesis of Ag2S nanoparticles at room temperature and their characterization with XPS].

Nanocrystalline silver sulfide was successfully synthesized at room temperature and ambient pressure via a novel, safe, convenient and inexpensive redox reaction, using silver oxide, sulfur and polyformaldehyde as reactants and ethylenediamine as solvent. The products were characterized with XPS, XRD and TEM. XRD spectrum demonstrates a monoclinic Ag2S; TEM shows the products are rod-like nanoparticles with average diameter of 100 nm, its corresponding SAED reveals clear diffraction spots indexed as (120) and (303); XPS confirms the formation of Ag2S and indicates the sample's surface stoichiometry of Ag:S=1:0.

[Chemical modification on the surface of nano-particles of ZnO and its characterization].

After nano-particles (ZnO) had been encapsulated by a kind of water-soluble cellulose Hydoxyl-Propyl-Methyl Cellulose (HPMC), then methyl methacrylate was grafted onto the surface of them. Thus the surface of nano-ZnO had been successfully modified. FTIR, DTA and TEM were utilized to confirm the results.

[Synthesis of polymeric drug nanomicrospheres containing probenecid].

Nonsteroidal antiinflammatory drug, probenecid, was covalently linked with 2-hydroxyethyl methacrylate (HEMA). The drug linked HEMA(abbreviated as HP) can be copolymerized with methy methacrylate (MMA) to obtain polymeric drug nanomicrospheres in ethanol/water system. Polymers were characterized with 1H-NMR, FTIR, GPC and TEM.