On the Strength of a 316L-Type Stainless Steel Subjected to Cold or Warm Rolling Followed by Annealing.

The ultrafine-grained microstructures and their effect on the yield strength of a 316L-type austenitic stainless steel processed by large strain cold/warm rolling and subsequent annealing were studied. A kind of continuous recrystallization developed during annealing, resulting in the evolution of uniform ultrafine-grained microstructures with relatively high residual dislocation densities. The development of such microstructure at 973 K led to excellent combination of tensile properties including high yield strength (σ > 900 MPa) and satisfactory plasticity (δ > 15%).