The Overload Effect on the Crack Tip Damage Mechanism in a 7075 Aluminum Alloy.

In the serviced components of a 7075 aluminum alloy, the propagation of fatigue crack can be retarded because of the overload effect; however, the corresponding retardation mechanisms are complex. To provide further insights into the retardation mechanisms of 7075 aluminum alloys, this study addresses the crack tip damage response of a cracked 7075 aluminum alloy under an overload effect. Based on the dual-scale modeling approach and the damage-coupled crystal plasticity model, the effect of the microstructure of a 7075 aluminum alloy on the damage behavior ahead of the crack tip under an overload was studied.

An Approach for Predicting the Low-Cycle-Fatigue Crack Initiation Life of Ultrafine-Grained Aluminum Alloy Considering Inhomogeneous Deformation and Microscale Multiaxial Strain.

In this paper, a low-cycle-fatigue (LCF) crack initiation life prediction approach that explicitly distinguishes nucleation and small crack propagation regimes is presented for ultrafine-grained (UFG) aluminum alloy by introducing two fatigue indicator parameters (FIPs) at the grain level. These two characterization parameters, the deformation inhomogeneity measured by the standard deviation of the dot product of normal stress and longitudinal strain and the microscale multiaxial strain considering the non-proportional cyclic additional hardening and mean strain effect, were proposed and respectively regarded as the driving forces for fatigue nucleation and small crack propagation. Then, the nucleation and small crack propagation lives were predicted by correlating these FIPs with statistical variables and cyclic J-integrals, respectively.