Ni-B-PTFE Nanocomposite Co-Deposition on the Surface of 2A12 Aluminum Alloy.

The spinning cup, a crucial component of textile equipment, relies heavily on 2A12 aluminum alloy as its primary raw material. Commonly, electroplating and chemical nickel-phosphorus (Ni-P) plating are employed to improve the surface characteristics of the object. Nevertheless, due to the growing expectations for the performance of aluminum alloys, the hardness and wear resistance of Ni-P coatings are no longer sufficient to fulfill industry standards.

Preparation of a Ni-P-nanoPTFE Composite Coating on the Surface of GCr15 Steel for Spinning Rings via a Defoamer and Transition Layer and Its Wear and Corrosion Resistance.

In this study, a method of preparing a Ni-P-nanoPTFE composite coating on the surface of GCr15 steel for spinning rings is proposed. The method incorporates a defoamer into the plating solution to inhibit the agglomeration of nano-PTFE particles and pre-deposits a Ni-P transition layer to reduce the possibility of leakage coating. Meanwhile, the effect of varying the PTFE emulsion content in the bath on the micromorphology, hardness, deposition rate, crystal structure, and PTFE content of the composite coatings was investigated.