A study on the physicochemical properties of surface modified Ti13Nb13Zr alloy for skeletal implants.

As it is widely stated in the literature, biofilms are responsible for most chronic infections, which have grown exponentially over the past three decades. The use of so-called alloys, as a new generation of materials, enables us to find the golden mean in the arena widely known as implantology. The use of the surface layer, using the chosen Atomic Layer Deposition method, is to be the basis for minimizing the risk of an organism reactions.

Functional Properties of Polyurethane Ureteral Stents with PLGA and Papaverine Hydrochloride Coating.

Despite the obvious benefits of using ureteral stents to drain the ureters, there is also a risk of complications from 80-90%. The presence of a foreign body in the human body causes disturbances in its proper functioning. It can lead to biofilm formation on the stent surface, which may favor the development of urinary tract infections or the formation of encrustation, as well as stent fragmentation, complicating its subsequent removal.

Selected Physicochemical Properties of Diamond Like Carbon (DLC) Coating on Ti-13Nb-13Zr Alloy Used for Blood Contacting Implants.

Despite high interest in the issues of hemocompatibility of titanium implants, particularly those made of the Ti-13Nb-13Zr alloy, the applied methods of surface modification still do not always guarantee the physicochemical properties required for their safe operation. The factors that reduce the efficiency of the application of titanium alloys in the treatment of conditions of the cardiovascular system include blood coagulation and fibrous proliferation within the vessel's internal walls. They result from their surfaces' physicochemical properties not being fully adapted to the specifics of the circulatory system.

Phase composition and morphology characteristics of ceria-stabilized zirconia powders obtained via sol-gel method with various pH conditions.

Purpose: High purity, fine crystalline, degradation-free at low temperature powders have attracted special interest in CAD/CAM prosthetic dentistry full ceramic restorations. This study reports the preparation and characterisation of zirconia-ceria (0.9 ZrO2 0.

sZrO2-CeO2 ceramic powders obtained from a sol-gel process using acetylacetone as a chelating agent for potential application in prosthetic dentistry.

Purpose: The main objective of this study was to obtain single-phase β-ZrO2 powders with so-called soft agglomerates reproducibile morphology with acetyl-acetone as a chelating-agent. To the best of our knowledge there is no avaiable data which determine the effect of acetyl acetone on the phase composition and morphology of ceria-doped ZrO2 powders for biomedical applications.

Methods: Twenty variants of powders with different water to zirconia precursor and acetylacetone to zirconia precursor molar ratios were prepared.

Evaluation of physicochemical properties of SiO2-coated stainless steel after sterilization.

The study of most of the literature devoted to the use of coronary stents indicates that their efficiency is determined by the physicochemical properties of the implant surface. Therefore, the authors of this study suggested conditions for the formation of SiO2 layers obtained with the use of sol-gel methodology showing physicochemical properties adequate to the specific conditions of the cardio-vascular system. Previous experience of authors helped them much to optimize the coating of 316LVM steel surface with SiO2.

Characterization of magnesia-doped yttria-stabilized zirconia powders for dental technology applications.

Purpose: This paper is focused on the works concerning preparation of zirconium oxide ceramic blocks recommended for CAD/CAM systems used in prosthetic dentistry for manufacturing fixed prosthetic restorations.

Methods: Zirconium-yttrium-magnesium mixed ceramic oxides were prepared by sol-gel method via hydrolysis and condensation of zirconium alkoxide precursor (zirconium (IV) propoxide) with yttrium and magnesium nitrates diluted in 2-propanol. The aim of this work was to obtain 2% mol yttria-stabilized zirconia ceramic powders with magnesium as an additional tetragonal ZrO2 phase stabilizer in amount between 2÷6% mol (with 2% variable).

The effects of a SiO2 coating on the corrosion parameters cpTi and Ti-6Al-7Nb alloy.

The aim of this paper was to evaluate the usefulness of the sol-gel method application, to modificate the surface of the Ti6Al7Nb alloy and the cpTi titanium (Grade 4) with SiO2 oxide, applied on the vascular implants to improve their hemocompatibility. Mechanical treatment was followed by film deposition on surface of the titanium samples. An appropriate selection of the process parameters was verified in the studies of corrosion, using potentiodynamic and impedance method.

Influence of surgical drills wear on thermal process generated in bones.

The influence of the wear rate of drills used in bone surgery on the temperature distribution in the femur models (Sawbones) is presented in the paper. Surgical drills of diameter d = 4.5 mm and diverse edge geometry (90° and 120°) were selected for the study.

Numerical and experimental analyses of drills used in osteosynthesis.

This paper presents the results of numerical analysis and experimental studies of the process of bone drilling using drills applied in osteosynthesis procedures. In the studies, two surgical drills with a diameter d = 4.5 mm and varying in drill point geometry 2κ were used.