Adsorption Recycling and High-Value Reutilization of Heavy-Metal Ions from Wastewater: As a High-Performance Anode Lithium Battery.

The dazzling adsorbent products make people overlook the harm of heavy metals adsorbed on them. Hazardous waste adsorbents cause secondary pollution. In this study, waste lignocellulose was dissolved by alkaline urea solvent and high-intensity ultrasound, then cross-linked by epichlorohydrin to make hydrogel, which was utilized to adsorb toxic heavy-metal wastewater.

Eu-Doped Zeolitic Imidazolate Framework-8 Modified Mixed-Crystal TiO for Efficient Removal of Basic Fuchsin from Effluent.

Zeolitic imidazolate framework-8 (ZIF-8) was doped with a rare-earth metal, Eu, using a solvent synthesis method evenly on the surface of a mixed-crystal TiO(Mc-TiO) structure in order to produce a core-shell structure composite ZIF-8(Eu)@Mc-TiO adsorption photocatalyst with good adsorption and photocatalytic properties. The characterisation of ZIF-8(Eu)@Mc-TiO was performed via X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Brunauer-Emmett-Teller analysis (BET) and ultraviolet-visible light differential reflectance spectroscopy (UV-DRs). The results indicated that Eu-doped ZIF-8 was formed evenly on the Mc-TiO surface, a core-shell structure formed and the light-response range was enhanced greatly.

Lignocellulose-Based Superabsorbent Polymer Gel Crosslinked with Magnesium Aluminum Silicate for Highly Removal of Zn (II) from Aqueous Solution.

Lignocellulose (LCE) was ultrasonically treated and intercalated into magnesium aluminum silicate (MOT) clay to prepare a nano-lignocellulose magnesium aluminum silicate polymer gel (nano-LCE-MOT) for the removal of Zn (II) from aqueous solution. The product was characterised using nitrogen adsorption/desorption isotherm measurements, Fourier-transform infrared spectroscopy, scanning electron microscopy and energy-dispersive X-ray spectroscopy. The conditions for the adsorption of Zn (II) on nano-LCE-MOT were screened, and adsorption kinetics and isotherm model analysis were carried out to explore the adsorption mechanism and achieve the optimal adsorption of Zn (II).

Enhanced heavy metal removal from an aqueous environment using an eco-friendly and sustainable adsorbent.

Thiol-lignocellulose sodium bentonite (TLSB) nanocomposites can effectively remove heavy metals from aqueous solutions. TLSB was formed by using -SH group-modified lignocellulose as a raw material, which was intercalated into the interlayers of hierarchical sodium bentonite. Characterization of TLSB was then performed with BET, FTIR, XRD, TGA, PZC, SEM, and TEM analyses.

Lignocellulose@ Activated Clay Nanocomposite with Hierarchical Nanostructure Enhancing the Removal of Aqueous Zn(II).

A lignocellulose@ activated clay (Ln@AC) nanocomposite with a hierarchical nanostructure was successfully synthesized by the chemical intercalation reaction and applied in the removal of Zn(II) from an aqueous solution. Ln@AC was characterized by N adsorption/desorption isotherms and X-Ray Diffraction (XRD), scanning Electron Microscope (SEM), transmission Electron Microscopy (TEM) and Fourier Transform Infrared Spectroscopy (FTIR) analysis, and the results indicate that an intercalated-exfoliated hierarchical nanostructure was formed. The effects of different adsorption parameters on the Zn(II) removal rate (weight ratio of Ln to AC, Ln@AC dosage, initial Zn(II) concentration, pH value, adsorption temperature, and time) were investigated in detail.

Nano@lignocellulose intercalated montmorillonite as adsorbent for effective Mn(II) removal from aqueous solution.

This paper describes the preparation of nano@lignocellulose (nano@LC) and a nano@lignocellulose/montmorillonite (nano@LC/MT) nanocomposite, as well as the capacity of the nano@LC/MT for adsorbing manganese ions from aqueous solution. The structure of nano@LC and nano@LC/MT was characterised by Fourier-transform infrared spectroscopy, X-ray diffraction, Scanning electron microscopy, and Transmission electron microscopy, which revealed that the diffraction peak of montmorillonite almost disappeared, infrared bands of the functional groups shifted, and morphology of the material changed after the formation of the composite. The optimum conditions for the adsorption of Mn(II) on the nano@LC/MT nanocomposite were investigated in detail by changing the initial Mn(II) concentration, pH, adsorption temperature, and time.