Formation Mechanism and Cohesive Energy Analysis of Metal-Coated Graphene Nanocomposites Using In-Situ Co-Reduction Method.

Nanocomposite powders based on metal-coated graphene were synthesized using an in-situ co-reduction method in order to improve wettability and interfacial bonding between graphene and metal. Graphene oxide (GO) of 2~3 atomic layers was synthesized using the Hummer's method with graphite as a raw material and then dispersed into a dispersing agent solution mixed with -Methyl pyrrolidone and deionized water to form a homogeneous GO suspension, which was finally added into electroless plating solutions for the reduction process. Copper-coated graphene (Cu@graphene) and nickel-coated graphene (Ni@graphene) were synthesized using this one-step and co-reduction method by mixing salt solutions containing metal ions and GOs into the plating solution.