Synthesis and Evaluation of Self-Assembled Azido Monolayer as a Novel Dielectric Layer for Fabricating Pentacene-Based Organic Thin Film Transistors.

Self-assembled 3-azidopropyltriethoxysilane monolayer (SAM) is used as a dielectric layer to modify the interface between the silicon dioxide wafer and the pentacene semiconductor layer in an organic thin film transistor (OTFT), Au/pentacene/3-azidopropyltriethoxysilane/SiO2/Si. Compared to the commonly used alkyl siliane C18 dielectric, 3-azidopropyltriethoxysilane which possesses stable formal charges is far more effective in increasing the ON/OFF ratio of OTFT device with an improvement of nearly three orders of magnitude. Analysis and measurements reported in this paper have illustrated for the first time the improvement of OTFT performance by a SAM compound with stable formal charges.

Organic thin-film-transistor Au/poly(3-hexylthiophene)/ (bilayer dielectrics)/Si having carbon nanotubes chemically bonded to poly(3-hexylthiophene) in the active layer.

Using poly(3-hexylthiophene) (P3HT) covalently bonded with carbon nanotubes (CNT) as an active layer in a bottom-gate/top contact, Au/(P3HT)/(bilayer dielectric)/Si OTFT device has resulted in an enhanced charge transport. The CNTs were firstly functionalized via ligand exchange with ferrocene, next lithiated by sec-butyllithium (s-BuLi) and then linked anionically with P3HT which has been synthesized via the modified Grignard metathesis method. Compared to the pristine P3HT, the CNTs-containing P3HT composite material has a higher energy level of HOMO and a smaller electrochemical bandgap E(g)(chem).