Bridging steady-state and stick-slip fracture propagation in glassy polymers.

Both an experimental and a theoretical investigation of fracture propagation mechanisms acting at the process zone scale in glassy polymers are presented. The main aim is to establish a common modeling for different kinds of glassy polymers presenting either steady-state fracture propagation or stick-slip fracture propagation or both, depending on loading conditions and sample shapes. From the experimental point of view, new insights are provided by the AFM measurements of viscoplastic strain fields acting within the micrometric process zone in a brittle epoxy resin, which highlight an extremely slow unexpected steady-state regime with finite plastic strains of about 30% around a blunt crack tip, accompanied by propagating shear lips.