Intraoral mineralization of abraded dental enamel.

The iodide permeability (Ip) of abraded bovine enamel increased after short exposure to an acid buffer and decreased after short exposure to a mineralizing solution. Intraoral exposure gave a marked decrease in Ip after one h and a continued lesser decrease after two and three h. In vitro exposure to fresh and dialyzed saliva and various undersaturated solutions indicated that the intraoral decrease was due to mineralization rather than to pellicle formation.

Effect of initial demineralization on the permeability of human tooth enamel to iodide.

Blocks of intact human enamel were exposed for four successive periods of 5 min to 2 ml of 10(-2) M K-acetate at pH 4.0, 4.5 and 5.

Dental fluorosis as related to the concentration of fluoride in teeth and bone.

Rats (N = 58), given a diet low in fluoride, were stomach-fed solutions of NaF and (NH4)3AIF6 in amounts corresponding to 3.3, 8.3, and 16.

Lead in enamel and saliva, dental caries and the use of enamel biopsies for measuring past exposure to lead.

Enamel biopsies taken from schoolchildren in a community where exposure to lead was a health hazard were analyzed for lead and fluoride. The children with high enamel lead had significantly higher caries scores than the children with low enamel lead, in spite of the fact that the high lead group also was higher in enamel fluoride. There was no increase in enamel lead with age.