Effect of Internal Support on the Tensile Properties and Fracture Mode of 304 Stainless Steel Thin-Walled Tubes.

Steel-tube composite structures contain multiple tubular components under tension. The enhancement of the mechanical properties of tubes under ultimate operating conditions is crucial for improving structural safety. In this study, 110 pieces of 304 stainless steel thin-walled tubes (SSTWTs) under five internal support conditions are investigated.

Corrosion Fatigue Fracture Characteristics of FSW 7075 Aluminum Alloy Joints.

The corrosion fatigue properties and fracture characteristics of friction stir welding joints of 7075 aluminum alloys were studied via corrosion fatigue tests, electrochemical measurements, and corrosion fatigue morphology and microstructure observations. The results show that the corrosion fatigue crack of the friction stir welding (FSW) joint of 7075 aluminum alloys originated in the junction zone between the thermomechanically affected zone and the weld nugget zone. The corrosion fatigue life of the joint decreased with increasing stress amplitude, with an S-N curve equation of lgN = 5.

Copper(II)-hydroxide facilitated C-C bond formation: the carboxamido pyridine system the methylimino pyridine system.

A copper(ii)-hydroxide-induced carbon-carbon bond formation reaction is explored with the synthesis of an asymmetric carboxamido-methylimino pyridine Cu(i) complex of [CuI(py(N-C[double bond, length as m-dash]O)(N[double bond, length as m-dash]C-C)ph2Me2)2]- (12). Two imine-methyl groups are coupled to form a bridged C-C bond (N[double bond, length as m-dash]C-C-C-C[double bond, length as m-dash]N) at the methyl positions with the reduction of two Cu2+ center ions to Cu+. The reaction is checked with three dicarboxamido pyridine [CuII-OH] complexes, with which dinuclear Cu(i) complexes of [Cu2(py(N-C[double bond, length as m-dash]O)2ph2R2)2]2- (R = methyl (3), methyl and allyl (6)) and trinuclear [CuII-CuI-CuII] complex of [Cu3(⊂20-py(N-C[double bond, length as m-dash]O)2ph2dienMe3)2]+ (9) are obtained.

Research on Residual Stress of a BS700 Butt-Welded Box Section and Its Influence on the Stability of Axial Compression Members.

BS700 high-strength steel is widely used in engineering. Welding residual stress during the manufacturing process has a significant influence on the structural safety and service life of steel structures. In this study, the residual stress of a BS700 butt-welded box section axial compression member was studied by the blind-hole method, its distribution law was summarized, and a residual stress distribution model was established.