Research on Enhancing the Comprehensive Performance of Fir Wood through Chemical Modification with a Biobased Unsaturated Polyester.

Fir wood was modified using epoxy soybean oil, diethylene glycol, and maleic anhydride as raw materials to enhance its mechanical properties, thermal stability, and water resistance. Diethylene glycol first opens the epoxy ring of the soybean oil and then reacts with maleic anhydride to produce an esterification reaction. The product modifies the fir wood through a chemical impregnation method.

Enhanced Modification of Fast-Growing Wood: Application and Evaluation of Castor Oil-Based Unsaturated Polyester Resin.

A type of multifunctional maleic acid ester monomer (COEGMA) was synthesized using castor oil as raw material, and green wood-plastic composites were prepared by chemically impregnating and curing the monomer into wood. The structure of the synthesized products at various stages was determined by FT-IR spectroscopy, H NMR, and GPC, and the curing experimental conditions were optimized. The results show that the water absorption of wood-plastic composites treated with COEGMA is reduced from the original 167.

Chemical Degradation of Waste PET and Its Application in Wood Reinforcement and Modification.

In recent years, with the increasing scarcity of fossil resources and the worsening environmental pollution, the effective utilization of wood and plastic waste has become a critical issue. In this paper, propylene glycol (PG) was used as an alcoholysis agent to degrade waste poly(ethylene terephthalate) (PET), and unsaturated polyester (UPR) was synthesized by the polycondensation reaction. The Chinese fir was modified by chemical impregnation to obtain a new type of waste PET-based wood-plastic composites.