Soldering of Passive Components Using Sn Nanoparticle Reinforced Solder Paste: Influence on Microstructure and Joint Strength.

In this study, the effects of adding Sn nanopowder (particle size < 150 nm) to three solder pastes SAC3-X(H)F3+, SCAN-Ge071-XF3+, and water washable WW50-SAC3 are evaluated regarding microstructure, morphology, joint strength, and electrical resistance. The nanopowder was added at a rate of 10% by weight and then mechanically mixed until homogenous solder paste was obtained. The results showed that the addition of Sn nanoparticles resulted in homogenous bond formation for SAC-3 and SCAN, while voids and bubbles formation slightly increased within the joint interface for the water washable solder paste.