Structural characterization of nanostructured Fe-8P powder mixture.

Nanostructured Fe-8P (wt%) powder mixture was prepared by high energy ball milling in a planetary ball mill (Fritsch P7) under argon atmosphere. The morphology of the particles, the phase identification and the alloying evolution process as a function of milling time are studied by scanning electron microscopy (SEM), X-ray diffraction (XRD) and 57Fe Mössbauer spectrometry (MS), respectively. Refinement based on Rietveld method of the XRD patterns and the Mössbauer spectra analysis show that the Fe(x)P (1 < x < 2) and Fe2P phosphide phases are the main product after 3 h of milling (approximately 10%).