Correlation between polymerization stress and interfacial integrity of composites restorations assessed by different in vitro tests.

Objective: to correlate polymerization stress data obtained under two compliance conditions with those from different interfacial quality tests.

Methods: Six commercial composites were tested (Filtek Z250/3M ESPE, Heliomolar/Ivoclar Vivadent, Aelite LS Posterior/Bisco, Filtek Supreme/3M ESPE, ELS/Saremco and Venus Diamond/Heraeus Kulzer). Bond strength (BS) was evaluated by push-out test on slices of bovine dentin (2-mm thick) with tapered cavities.

Influence of the base and diluent monomer on network characteristics and mechanical properties of neat resin and composite materials.

This study evaluated the effect of the combination of two dimethacrylate-based monomers [bisphenol A diglycidyl dimethacrylate (BisGMA) or bisphenol A ethoxylated dimethacrylate (BisEMA)] with diluents either derived from ethylene glycol dimethacrylate (ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate) or 1,10-decanediol dimethacrylate (D3MA) on network characteristics and mechanical properties of neat resin and composite materials. The degree of conversion, maximum rate of polymerization and water sorption/solubility of unfilled resins and the flexural strength and microhardness of composites (after 24 h storage in water and 3 months storage in a 75 vol% ethanol aqueous solution) were evaluated. Data were analyzed with two-way ANOVA and Tukey's test (α = 0.

Monomers used in resin composites: degree of conversion, mechanical properties and water sorption/solubility.

The organic phase of resin composites is constituted by dimethacrylate resins, the most common monomers being the bisphenol A diglycidildimethacrylate (BisGMA), its ethoxylated version (BisEMA), triethylene glycol dimethacrylate (TEGDMA) and urethane dimethacrylate (UDMA). This study compared the homopolymers formed from the monomers used in restorative dental composites in terms of their degree of conversion (DC) and reaction kinetics (by near infra-red spectroscopy, n=3), mechanical properties (flexural modulus and strength in three point-bending, FM and FS, respectively, n=15), water sorption and solubility (WS and SL, respectively - ISO 4049, n=5). Materials were made photopolymerizable by the addition of camphoroquinone/dimethylamine ethyl methacrylate.