Effect of photoinitiator concentration on marginal and internal adaptation of experimental composite blends photocured by modulated methods.

Objective: The aim of this study was to evaluate the influence of photoinitiator concentration on marginal and internal adaptation of composites photocured by modulated methods.

Materials And Methods: Composites based on BisGMA/triethylene glycol dimethacrylate and 65 wt% of filler were prepared with different concentrations of camphorquinone/amine (C1-0.5%, C2-1%, C3-1.

Effects of curing protocols on fluid kinetics and hardness of resin cements.

The effects of polymerization protocols on water sorption/solubility, the diffusion coefficient (D), the flux (J), and the hardness (KH) of two resin cements were evaluated. The materials were manipulated and divided into three groups (n=6) according to the curing protocol: PA=photoactivation (40 s); DP=delayed photoactivation (10 min self-curing plus 40 s photoactivated); CA=chemical activation. After desiccation, the specimens were weighed, stored in water (37ºC), evaluated over 28-days, and hardness recorded.

Bond strength and interfacial micromorphology of etch-and-rinse and self-adhesive resin cements to dentin.

Purpose: To evaluate the microtensile bond strength and interfacial micromorphology of indirect composite restorations to dentin using three commercial resin cements after 24 hours and 30 days of water storage.

Materials And Methods: The medium dentin of third human molars was exposed (N = 30, n = 10 per group). Three commercial resin cements were used to cement indirect resin composite restorations to dentin: the auto-cured C&B Cement/All Bond 2, the dual-cured RelyX ARC/Adper Single Bond 2, and the self-adhesive dual-cured RelyX Unicem.

Microtensile bond strength test and failure analysis to assess bonding characteristics of different adhesion approaches to ground versus unground enamel.

This study evaluated the bonding characteristics to ground and unground enamel obtained with different strategies. For this purpose, 24 sound third-molars were bisected mesiodistally to obtain tooth halves. A flat enamel area was delimited in the tooth sections, which were randomly distributed into 8 groups (n=6), according to the enamel condition (ground and unground) and adhesive system (Adper Single Bond 2 - SB2; Adper Prompt L-Pop - PLP; Adper Prompt - AD; Clearfil SE Bond - SE).

Microtensile bond strength of sealant and adhesive systems applied to occlusal primary enamel.

Purpose: To compare the microtensile bond strength (muTBS) of a self-etch adhesive system (OptiBond Solo Self-Etch Adhesive System), two total etch adhesive system (OptiBond FL; OptiBond Solo), and a conventional sealant (Clinpro) applied to the occlusal surface of primary molars under saliva contamination.

Methods: Sealant and adhesive systems were applied under manufacturers' specifications with or without previous saliva contamination. After storage in distilled water at 37 degrees C for 24 hours, the specimens were longitudinally sectioned perpendicularly to the adhesive interface to obtain sticks (0.