Comparison of acid exfoliators in carbon nanosheets synthesis from stinging nettle (Urtica dioica) for electrochemical applications.

Carbon nanosheets (CNs) were successfully synthesized from nettle stem (NS) which is an inexpensive material with a high carbon content that is abundantly available in nature. CNs were produced using chemical (potassium hydroxide activation and acid exfoliation) and thermal treatments. Sulfuric (HSO), phosphoric (HPO) and nitric (HNO) acid solutions were used for exfoliation.

Nitrogen self-doped activated carbons the direct activation of leaves for high energy density supercapacitors.

In this study, nitrogen self-doped activated carbons (ACs) obtained the direct activation of green leaves (SSLs) for high energy density supercapacitors were investigated. The SSL-derived direct-activated carbons (hereinafter referred to SD-ACs) were synthesized by impregnating sodium hydroxide as an activating agent and heating up to 720 °C without a hydrothermal carbonization or pyrolysis step. The optimum condition was investigated by varying the weight ratio of raw SSLs to NaOH.

Preparation and electrochemical performance of nitrogen-enriched activated carbon derived from silkworm pupae waste.

In this study, nitrogen-enriched activated carbon from silkworm pupae waste (P-AC) was successfully prepared and its electrochemical performances in aqueous and organic electrolytes were investigated. Silkworm pupae waste is beneficial because it is a nitrogen-enriched, inexpensive, and locally available material. The preparation process includes hydrothermal treatment of the silkworm pupae waste at 200 °C, and chemical activation using zinc chloride at activation temperatures of 700, 800 and 900 °C (P700, P800, and P900, respectively).