Oxygen diffusion and surface exchange in the mixed conducting oxides SrTiFeO.

Oxygen transport in the mixed ionic-electronic conducting perovskite-oxides SrTiFeO (with y = 0.5 and y = 1.0) was studied by oxygen isotope exchange measurements.

Do dislocations act as atomic autobahns for oxygen in the perovskite oxide SrTiO3?

The transport properties of edge dislocations comprising a symmetrical 6° [001] tilt grain boundary in weakly acceptor-doped SrTiO3 were investigated by means of various experimental and computational techniques. Oxygen transport along the dislocation array was probed by means of (18)O/(16)O exchange experiments under (standard) oxidising conditions (pO2 = 5 × 10(-1) bar) and also under reducing conditions (pO2 = 7 × 10(-22) bar) at T = 973 K. In both cases, isotope profiles obtained by Secondary Ion Mass Spectrometry (SIMS) indicated no evidence of fast diffusion along the dislocation array.