Peculiarities of Fatigue Crack Growth in Steel 17H1S after Long-Term Operations on a Gas Pipeline.

This work presents the results of metallographic studies and the tensile, impact, and fatigue crack growth (FCG) resistance tests of 17H1S main gas pipeline steel in the as-received (AR) state and after a long-term operation (LTO). A significant number of non-metallic inclusions forming chains stretched along the direction of pipe rolling were found in the microstructure of the LTO steel. The lowest values of elongation at break and impact toughness of the steel were determined for the lower part of the pipe close to its inner surface.