Efficient removal of amoxicillin and paracetamol from aqueous solutions using magnetic activated carbon.

Activated carbon (AC)/CoFeO nanocomposites, MAC-1 and MAC-2, were prepared by a simple pyrolytic method using a mixture of iron(III)/cobalt(II) benzoates and iron(III)/cobalt(II) oxalates, respectively, and were used as efficient adsorbents for the removal of amoxicillin (AMX) and paracetamol (PCT) of aqueous effluents. The synthesized nanocomposites were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), vibrating sample magnetometry (VSM), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and transmission electron microscopy (TEM). The sizes of cobalt ferrite nanoparticles formed from benzoates of iron(III)/cobalt(II) and oxalates of iron(III)/cobalt(II) precursors were in the ranges of 5-80 and 6-27 nm, respectively.

Magnetic activated carbon-Fe3O4 nanocomposites--synthesis and applications in the removal of acid yellow dye 17 from water.

In this work, synthesis of activated carbon-Fe3O4 composites using activated carbon and iron benzoate/oxalate precursors by simple pyrolytic method and its utility for the removal of acid yellow dye from water are presented. Iron carboxylates held up into the pores of carbon dissociate at their decomposition temperatures form dispersed Fe3O4 nanoparticles in carbon matrix. The composites were characterized by FTIR, PXRD, SEM, TEM, EDX and magnetization measurements.

Synthesis of magnetic activated carbon/α-Fe2O3 nanocomposite and its application in the removal of acid yellow 17 dye from water.

The adsorption of acid yellow 17 dye on activated carbon/α-Fe2O3 nanocomposite prepared by simple pyrolytic method using iron(II) gluconate was investigated by batch technique. The composite was characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), and vibrating sample magnetometry (VSM). The size of iron oxide nanoparticles formed from iron(II) gluconate precursor is in the range 5-17nm.