Amphoteric Be in GaN: Experimental Evidence for Switching between Substitutional and Interstitial Lattice Sites.

We show that Be exhibits amphoteric behavior in GaN, involving switching between substitutional and interstitial positions in the lattice. This behavior is observed through the dominance of Be_{Ga} in the positron annihilation signals in Be-doped GaN, while the emergence of V_{Ga} at high temperatures is a consequence of the Be impurities being driven to interstitial positions. The similarity of this behavior to that found for Na and Li in ZnO suggests that this could be a universal property of light dopants substituting for heavy cations in compound semiconductors.

Evaluation of the concentration of point defects in GaN.

Photoluminescence (PL) was used to estimate the concentration of point defects in GaN. The results are compared with data from positron annihilation spectroscopy (PAS), secondary ion mass spectrometry (SIMS), and deep level transient spectroscopy (DLTS). Defect-related PL intensity in undoped GaN grown by hydride vapor phase epitaxy increases linearly with the concentration of related defects only up to 10 cm.

Identification of vacancy defect complexes in transparent semiconducting oxides ZnO, In2O3 and SnO2.

Positron annihilation spectroscopy, when combined with supporting high-quality modeling of positron states and annihilation in matter, is a powerful tool for detailed defect identification of vacancy-type defects in semiconductors and oxides. Here we demonstrate that the Doppler broadening of the positron annihilation radiation is a very sensitive means for observing the oxygen environment around cation vacancies, the main open-volume defects trapping positrons in measurements made for transparent semiconducting oxides. Changes in the positron annihilation signal due to external manipulation such as irradiation and annealing can be correlated with the associated changes in the sizes of the detected vacancy clusters.