An Inhibitor-Loaded LDH- and MOF-Based Bilayer Hybrid System for Active Corrosion Protection of Aluminum Alloys.

A novel inhibitor-loaded bilayer hybrid system based on the LDH inner layer and MOF outer layer is designed on an aluminum alloy 2A12 surface to improve corrosion performance. The hybrid film system covers the inherent cavities and intercrystalline defects of the LDH film using the affinity between the LDH and the MOF compounds. The results demonstrate that the LDH-I precursor film is entirely covered by new Zn-based MOF microrods.

ADOR zeolite with 12 × 8 × 8-ring pores derived from IWR germanosilicate.

Zeolites have been well known for decades as catalytic materials and adsorbents and are traditionally prepared using the bottom-up synthesis method. Although it was productive for more than 250 zeolite frameworks, the conventional solvothermal synthesis approach provided limited control over the structural characteristics of the formed materials. In turn, the discovery and development of the Assembly-Disassembly-Organization-Reassembly (ADOR) strategy for the regioselective manipulation of germanosilicates enabled the synthesis of previously unattainable zeolites with predefined structures.

Vapour-phase-transport rearrangement technique for the synthesis of new zeolites.

Owing to the significant difference in the numbers of simulated and experimentally feasible zeolite structures, several alternative strategies have been developed for zeolite synthesis. Despite their rationality and originality, most of these techniques are based on trial-and-error, which makes it difficult to predict the structure of new materials. Assembly-Disassembly-Organization-Reassembly (ADOR) method overcoming this limitation was successfully applied to a limited number of structures with relatively stable crystalline layers (UTL, UOV, *CTH).

Insight into the ADOR zeolite-to-zeolite transformation: the UOV case.

IPC-12 zeolite is the first member of the ADOR family produced by the structural transformation of UOV. The details of the UOV rearrangement were studied to determine the influence of the properties of the parent zeolite and treatment conditions on the outcome of IPC-12 formation. It was established that incomplete disassembly of UOV can be caused by insufficient lability of interlayer connectivity in the parent material possessing Si-enriched D4Rs or by inhibition of hydrolysis by diluted acid at high temperature.

Methane adsorption in ADOR zeolites: a combined experimental and DFT/CC study.

Physical adsorption of methane in purely siliceous molecular sieves prepared by a recently discovered synthetic pathway using 2D zeolites as nanoscale building blocks has been investigated by means of combined experimental and theoretical approaches. The DFT/CC-based method has been tested on ADOR zeolites of the UTL family and a few experimentally well-characterized siliceous zeolites. Excellent agreement between theoretical and experimental heats of adsorption has been found for OKO, PCR, MFI, CHA and AEI zeolites.