The tradeoffs associated with modular hip prostheses.

In an effort to gain greater insight into the tradeoffs associated with modular hip prostheses, 2 approaches were taken. A questionnaire was sent to each of the orthopaedic implant manufacturing companies asking specific questions regarding modular components, and a series of retrieved prostheses, both modular and nonmodular, were examined to determine the potential sources of problems associated with modular connections. The respondents to the questionnaire generally agreed that it was more expensive to produce modular prostheses due to the required tolerances at the modular connections, and that the increased flexibility provided by the modularity was important to surgical outcome.

Loss of hydroxyapatite coating on retrieved, total hip components.

The goal of this study was to examine the early retrievals of hydroxyapatite-(HA) coated hip prostheses to assess evidence of osteoconductivity, resorption of HA, and the integrity of the HA/implant bond. Six retrieved HA-coated hip prostheses (3 femoral hip stems, 3 acetabular cups) were analyzed for the amount of bone ongrowth or ingrowth of the HA-coated surface and the extent to which the coating was still present after in vivo service. The examination of these six HA-coated prostheses indicates that HA appeared to be osteoconductive.

Failure of a well-fixed bone-ingrown titanium hip prosthesis.

A cementless titanium femoral stem was revised 5 years after implantation because of acute pain and progressive osteolysis. Substantial amounts of titanium and polyethylene wear debris were found in the surrounding tissues. Multiple sources of this debris were found as well as detachment of titanium fiber-mesh pads from the body of the femoral stem.

Interfaces between host and uncemented femoral hip prostheses.

The authors analyzed 200 uncemented hip prostheses that were retrieved. They determined the type and extent of host-implant interfaces, but found little correlation between subjective pain relief and the histology of the interfaces. Wear debris, bone resorption and looseness were related to pain, although even with these the relationship was not statistically significant.