Micromechanical modelling for bending behaviour of novel bioinspired alumina-based dental composites.

The clinical failure mode of dental crown ceramics involves radial cracking at the interface, driven by the surface tension generated from the flexure of the ceramic layer on the subsurface. This results in a reduced lifespan for most all-ceramic dental crowns. Therefore, investigating optimal material combinations to reduce stress concentration in dental crown materials has become crucial for future successful clinical applications.

Bio-inspired nacre-like zirconia/PMMA composites for chairside CAD/CAM dental restorations.

Objectives: To introduce a versatile fabrication process to fabricate zirconia/PMMA composites for chairside CAD/CAM dental restorations. These zirconia composites have nacre-like lamellar microstructures, competent and tooth-matched mechanical properties, as well as crack resistance behaviours.

Methods: Bi-directional freeze casting was used to fabricate ceramic green bodies with highly aligned lamellar structure.

Biomimetic Nacre-like Hydroxyapatite/Polymer Composites for Bone Implants.

One of the most ambitious goals for bone implants is to improve bioactivity, incapability, and mechanical properties; to reduce the need for further surgery; and increase efficiency. Hydroxyapatite (HA), the main inorganic component of bones and teeth, has high biocompatibility but is weak and brittle material. Cortical bone is composed of 70% calcium phosphate (CaP) and 30% collagen and forms a complex hierarchical structure with anisotropic and lamellar microstructure (osteons) which makes bone a light, strong, tough, and durable material that can support large loads.