Microscale chemical imaging to characterize and quantify corrosion processes at the metal-electrolyte interface.

We introduce an experimental setup to chemically image corrosion processes at metal-electrolyte interfaces under stagnant, confined conditions-relevant in a wide range of situations. The setup is based on a glass capillary, in which precipitation of corrosion products in the interfacial aqueous phase can be monitored over time with optical microscopy, and chemically and structurally characterized with microscopic synchrotron-based techniques (X-ray fluorescence, X-ray diffraction, and X-ray absorption spectroscopy). Moreover, quantification of precipitates through X-ray transmission measurements provides in-situ corrosion rates.

Speciation Controls the Kinetics of Iron Hydroxide Precipitation and Transformation at Alkaline pH.

The formation of energetically favorable and metastable mineral phases within the Fe-HO system controls the long-term mobility of iron complexes in natural aquifers and other environmentally and industrially relevant systems. The fundamental mechanism controlling the formation of these phases has remained enigmatic. We develop a general partial equilibrium model, leveraging recent synchrotron-based data on the time evolution of solid Fe(III) hydroxides along with aqueous complexes.

Chloride-induced corrosion of steel in concrete-insights from bimodal neutron and X-ray microtomography combined with ex-situ microscopy.

Unlabelled: The steel-concrete interface (SCI) is known to play a major role in corrosion of steel in concrete, but a fundamental understanding is still lacking. One reason is that concrete's opacity complicates the study of internal processes. Here, we report on the application of bimodal X-ray and neutron microtomography as in-situ imaging techniques to elucidate the mechanism of steel corrosion in concrete.

Transformation of 2-Line Ferrihydrite to Goethite at Alkaline pH.

The transformation of 2-line ferrihydrite to goethite from supersaturated solutions at alkaline pH ≥ 13.0 was studied using a combination of benchtop and advanced synchrotron techniques such as X-ray diffraction, thermogravimetric analysis, and X-ray absorption spectroscopy. In comparison to the transformation rates at acidic to mildly alkaline environments, the half-life, , of 2-line ferrihydrite reduces from several months at pH = 2.

Diffusion potentials in saturated hardened cement paste upon chloride exposure.

The diffusion potentials can cause significant errors in corrosion-related investigations of reinforced concrete structures (half-cell potential mapping, potentiometric sensors). Therefore, an improved understanding of the diffusion potentials in cement-based materials is needed. This study investigates the permselective behavior and its implication for the arising diffusion potentials.