Effect of annealing treatment on the crystallisation and leaching of dumped base metal smelter slags.

Leaching tests of base metals contained in two smelter slags were undertaken in ammonia and nitric acid solutions aiming to recover Co, Cu and Zn. Leaching tests were conducted at 25 and 60°C at pH=0 and 3 in HNO(3) and pH=12 in NH(4)OH media. XRD analysis revealed that the dumped slags were amorphous.

Cleaning of a copper matte smelting slag from a water-jacket furnace by direct reduction of heavy metals.

Cleaning experiments of a copper matte smelting slag from the water-jacket furnace was undertaken by direct reduction in a laboratory-scale electric furnace. The effects of coal-to-slag ratio, w, and the reduction time, t, were considered for two different coal/slag mixing procedures. In the first procedure, metallurgical coal was added to the molten slag, whereas in the second procedure, coal was premixed with the solid slag before charging into the furnace.