On the Anti-Corrosion Property of Dry-Gel-Conversion-Grown MFI Zeolite Coating on Aluminum Alloy.

MFI zeolite film coated on AA6061 alloy was prepared from fumed silica modified with/without n-octyldecyltrimethoxysilane (ODS) by means of dry gel conversion (DGC) method. The DGC-grown MFI zeolite film could form a strong barrier to protect AA6061 surface against the corrosion from NaCl solution. By using fumed silica as a starting material, the hydrophilicity and anti-corrosion capability of the MFI zeolite film declined with increasing humidity in the DGC synthesis.

Deliberate design of a 3D homochiral Cu(II)/l-met/Ag(I) coordination network based on the distinct soft-hard recognition principle.

A homochiral amino acid coordination network [{Ag3Cu3(l-methioninato)6(NO3)3(H2O)3}.7H2O]n, self-assembled from CuII, AgI, and l-methionine via a distinct soft-hard recognition process, shows interesting characteristics, in that it is constructed from 1D helical building blocks and contains homochiral channels in which 1D water chains are hosted. This result provides an effective and controllable strategy for the preparation of enantiopure heterometallic supramolecular structures that are relevant to biopolymers.