Evolution of Properties of High-Strength and High-Mg-Content CuMg Alloys After Being Subjected to Single Operation 50% Deformation in Hot and Cold Upsetting Tests.

Since most hot and cold metal-forming processes originate from various casting processes, it is important to test their susceptibility to the deformation of new materials. Cast rods of CuMg alloys with a Mg content of 2, 2.4, 2.

The Influence of Various Welding Methods on the Microstructure and Mechanical Properties of 316Ti Steel.

Austenitic stainless steels are very popular due to their high strength properties, ductility, excellent corrosion resistance and work hardening. This paper presents the test results for joining AISI 316Ti austenitic steel. The technologies used for joining were the most popular welding techniques such as TIG (welding with a non-consumable electrode in the shield of inert gases), MIG (welding with a consumable electrode in the shield of inert gases) as well as high-energy EBW welding (Electron Beam Welding) and plasma PAW (plasma welding).

Recycling of Hard Disk Drive Platters via Plastic Consolidation.

The paper presents the comparison of two methods of recycling aluminum from HDD platters-the melting method and the method of plastic consolidation. The main elements of HDD memory, i.e.

Recycling of Electrical Cables-Current Challenges and Future Prospects.

Civilization and technical progress are not possible without energy. Dynamic economic growth translates into a systematic increase in demand for electricity. Ensuring the continuity and reliability of electricity supplies is one of the most important aspects of energy security in highly developed countries.

Microstructure and Mechanical Properties of Al-Si Alloys Produced by Rapid Solidification and Hot Extrusion.

The paper presents the results of tests of rapid solidification (RS) aluminum alloys with the addition of silicon (5%, 11%, and 20%). Casting by melt-spinning on the surface of an intensively cooled copper cylinder allowed to obtain a metallic material in the form of flakes, which were then consolidated in the process of pressing and direct extrusion. The effect of refinement on structural components after rapid solidification was determined.

Research of Friction Stir Welding (FSW) and Electron Beam Welding (EBW) Process for 6082-T6 Aluminum Alloy.

The paper presents the results of the joining tests of the EN AW-6082 T6 alloy. The materials were joined using the EBW high-energy (electron beam welding) and friction stir welding (FSW) methods. In the case of FSW welding, the following parameters were used: the linear speed was 355 mm/min, and the rotational speed of the welding tool was 710.

Determining the Mechanical Properties of Solid Plates Obtained from the Recycling of Cable Waste.

In this article, the possibility of obtaining a solid plate from waste cable sheaths, by mechanical recycling, i.e., grinding, plasticising and pressing, is discussed-waste cable sheaths being pure PVC with a slight admixture of silicone.

Studies of Selective Recovery of Zinc and Manganese from Alkaline Batteries Scrap by Leaching and Precipitation.

Recovery of zinc and manganese from scrapped alkaline batteries were carried out in the following way: leaching in HSO and selective precipitation of zinc and manganese by alkalization/neutralization. As a result of non-selective leaching, 95.6-99.

Recovery of Non-Ferrous Metals from PCBs Scrap by Liquation from Lead.

This article presents the results of research on the recycling of non-ferrous metals from PCB scrap using melting in metallic lead. The idea of this process is to dissolve (transfer) metals from PCB scrap in lead, and then liquation them by cooling the lead-metals alloy. PCB scrap was crushed and then melted into liquid lead.

Effect of Various Forms of Aluminum 6082 on the Mechanical Properties, Microstructure and Surface Modification of the Profile after Extrusion Process.

This article presents a method of reusing aluminum scrap from alloy 6082 using the hot extrusion process. Aluminum chips from milling and turning processes, having different sizes and morphologies, were cold pressed into briquettes prior to hot pressing at 400 °C at a ram speed of 2 mm/s. The study of mechanical properties combined with observations of the microstructures, as well as tests of density, hardness and electrical conductivity were carried out.

The Pressure Compaction of Zr-Nb Powder Mixtures and Selected Properties of Sintered and KOBO-Extruded Zr-xNb Materials.

Materials were obtained from commercial zirconium powders. 1 mass%, 2.5 mass% and 16 mass% of niobium powders were used as the reinforcing phase.

The Extrusion and SPS of Zirconium-Copper Powders and Studies of Selected Mechanical Properties.

Zr-2.5Cu and Zr-10Cu powder mixtures were consolidated in the extrusion process and using the spark plasma sintering technique. In these studies, material tests were carried out in the fields of phase composition, microstructure, hardness and tensile strength for Zr-Cu materials at room temperature (RT) and 400 °C.

Zirconium Phase Transformation under Static High Pressure and ω-Zr Phase Stability at High Temperatures.

High-purity Zr has been observed to undergo a phase transformation from the α-phase to the hexagonal ω-phase under high pressure generated either statically or by shock loading. The transition pressure from α-Zr to ω-Zr at 300 K is 2.10 GPa.