The Performance of Nonwoven PLLA Scaffolds of Different Thickness for Stem Cells Seeding and Implantation.

The 3D reconstruction of 100 μm- and 600 μm-thick fibrous poly-L/L-lactide scaffolds was performed by confocal laser scanning microscopy and supported by scanning electron microscopy and showed that the density of the fibers on the side adjacent to the electrode is higher, which can affect cell diffusion, while the pore size is generally the same. Bone marrow mesenchymal stem cells cultured in a 600 μm-thick scaffold formed colonies and produced conditions for cell differentiation. An in vitro study of stem cells after 7 days revealed that cell proliferation and hepatocyte growth factor release in the 600 μm-thick scaffold were higher than in the 100 μm-thick scaffold.

Structural and mechanical characteristics of collagen tissue coated with chitosan in a liquid CO/water system at different pressures.

Chitosan coatings of biological heart-valve prostheses enhance their biocompatibility, resistance to pathogenic microflora and lifetime. Collagen tissues can be coated with chitosan in aqueous solution acidified, to make chitosan soluble, with HCO formed from a coexisting liquid CO phase under pressure. The advantage of HCO is that it can be easily removed after the coating procedure.