Morphological Evolution of Sn-Metal-Based Anodes for Lithium-Ion Batteries Using Operando X-Ray Imaging.

Sn-based electrodes are promising candidates for next-generation lithium-ion batteries. However, it suffers from deleterious micro-structural deformation as it undergoes drastic volume changes upon lithium insertion and extraction. Progress in designing these materials is limited to complex structures.

Complementing Graphenes: 1D Interplanar Charge Transport in Polymeric Graphitic Carbon Nitrides.

Charge transport in polymeric graphitic carbon nitrides is shown to proceed via diffusive hopping of electron and hole polarons with reasonably high mobilities >10(-5) cm(2) V(-1) s(-1). The power-law behavior of the ultrafast luminescence decay exhibits that the predominant transport direction is perpendicular to the graphitic polymer sheets, thus complementing 2D materials like graphene.

A molecular approach to self-supported cobalt-substituted ZnO materials as remarkably stable electrocatalysts for water oxidation.

In regard to earth-abundant cobalt water oxidation catalysts, very recent findings show the reorganization of the materials to amorphous active phases under catalytic conditions. To further understand this concept, a unique cobalt-substituted crystalline zinc oxide (Co:ZnO) precatalyst has been synthesized by low-temperature solvolysis of molecular heterobimetallic Co(4-x)Zn(x) O4 (x = 1-3) precursors in benzylamine. Its electrophoretic deposition onto fluorinated tin oxide electrodes leads after oxidative conditioning to an amorphous self-supported water-oxidation electrocatalyst, which was observed by HR-TEM on FIB lamellas of the EPD layers.

Metal-free photocatalytic graphitic carbon nitride on p-type chalcopyrite as a composite photocathode for light-induced hydrogen evolution.

Recently, it has been shown that an abundant material, polymeric carbon nitride, can produce hydrogen from water under visible-light irradiation in the presence of a sacrificial donor. We present herein the preparation and characterization of graphitic carbon nitride (g-C(3)N(4)) films on p-type semiconducting CuGaSe(2) chalcopyrite thin-film substrates by thermal condensation of a dicyandiamide precursor under inert-gas conditions. Structural and surface morphological studies of the carbon nitride films suggest a high porosity of g-C(3)N(4) thin films consisting of a network of nanocrystallites.