Effect of Grinding and Polishing Protocols on Surface Roughness, Flexural Strength, and Phase Transformation of High-Translucent 5 mol% Yttria-Partially Stabilized Zirconia.

Objectives:  This study evaluated surface roughness, biaxial flexural strength, and phase transformation of 5Y-PSZ after grinding and polishing with different protocols.

Material And Methods:  Two commercial 5Y-PSZ, Lava Esthetic (L) and Cercon xt (C), were used and divided into 3 groups: LC and CC represented unpolished control groups; LE and CE were polished with protocol I (EVE DIASYNT® PLUS HP following with EVE DIACERA RA); and LJ and CJ were polished with protocol II (Superfine diamond bur following with Jota ZIR Gloss polishing kit). Surface roughness was evaluated after polishing step-by-step with a contact-type profilometer.

Effect of ionizing radiation on the mechanical properties of current fluoride-releasing materials.

Objectives: This study aimed to evaluate the effect of fractional radiation on the mechanical properties of fluoride-releasing materials.

Materials And Methods: High-viscosity glass ionomer cement (F9), resin-modified glass ionomer cement (F2), glass hybrid restoration (EQ), and bioactive composite (AC) were divided into 3 subgroups: 0, 35, and 70 Gy fractional radiation doses. The specimens were subjected to surface roughness, Vickers microhardness, and compressive strength tests.

Calcium phosphate ceramic as a model for enamel substitute material in dental applications.

Objective: This study aimed to develop enamel substitute material using a mechanochemical technique.

Materials And Methods: Hydroxyapatite was synthesized with and without tricalcium phosphate under uniaxial pressing of 10 and 17 MPa (HA10, HA17, BCP10, and BCP17), followed by sintering at 1250 °C for 2 h. Human enamel and dentin blocks were used as control groups.