Influence of high-speed sintering protocols on translucency, mechanical properties, microstructure, crystallography, and low-temperature degradation of highly translucent zirconia.

Objectives: Impacts of high-speed sintering on the optical and mechanical properties, microstructure, crystallography, and low-temperature degradation of commercial yttria-partially stabilized zirconia (Y-PSZ) were investigated.

Methods: Five commercial Y-PSZ products (KATANA HT, KATANA STML, KATANA UTML, Zpex 4, and Zpex Smile) were investigated. Specimens were sintered following speed-sintering (~90 min) and conventional-sintering protocols (~7 h), and a group of KATANA STML was super-speed-sintered (18 min).

Influence of sintering conditions on translucency, biaxial flexural strength, microstructure, and low-temperature degradation of highly translucent dental zirconia.

There is limited research on the influence of different sintering temperatures on the properties of highly translucent zirconia ceramics. This study demonstrated the influence of different sintering temperatures on the translucency, crystallographic structure, biaxial flexural strength, microstructure, and low-temperature degradation (LTD) of three highly translucent zirconia grades, i.e.