Rotary-jet spun polycaprolactone/nano-hydroxyapatite scaffolds modified by simulated body fluid influenced the flexural mode of the neoformed bone.

Polycaprolactone (PCL) is a biocompatible, biodegradable synthetic polymer which in combination with nanohydroxyapatite (nHAp) can give rise to a low cost, nontoxic bioactive product with excellent mechanical properties and slow degradation. Here we produced, characterized and evaluated in vivo the bone formation of PCL/nHAp scaffolds produced by the rotary jet spinning technique. The scaffolds produced were firstly soaked into simulated body fluid for 21 days to also obtain nHAp onto PCL/nHAp scaffolds.

In vitro and in vivo evaluation of rotary-jet-spun poly(ɛ-caprolactone) with high loading of nano-hydroxyapatite.

Herein, poly(ɛ-caprolactone) (PCL) mats with different amounts of nanohydroxyapatite (nHAp) were produced using rotary-jet spinning (RJS) and evaluated in vitro and in vivo. The mean fiber diameters of the PCL, PCL/nHAp (3%), PCL/nHAp (5%), and PCL/nHAp (20%) scaffolds were 1847 ± 1039, 1817 ± 1044, 1294 ± 4274, and 845 ± 248 nm, respectively. Initially, all the scaffolds showed superhydrophobic behavior (contact angle around of 140C), but decreased to 80° after 30 min.