Comparison of Magnetron-Sputtered and Cathodic Arc-Deposited Ti and Cr Thin Films on Stainless Steel for Bipolar Plates.

In this work, the potential of magnetron sputtering, as well as cathodic arc evaporation, is investigated with regard to its suitability as a bipolar plate coating of a PEM fuel cell. For this purpose, Cr and Ti thin films were deposited onto a 0.1 mm SS316L by varying the power and bias voltage.

Bias Voltage Dependency of Structural and Bipolar Plate-Related Properties of Cathodic Arc-Deposited Carbon-Based Coatings.

Carbon-based coatings composed of a chromium interlayer and a carbon top layer were deposited on stainless steel substrates via cathodic arc evaporation. During the carbon deposition, the bias voltage was varied between 900 and 1 V to investigate the influence on the structural, electrical, and electrochemical properties. Raman spectroscopy indicated a dependency of the intensity ratio and G peak position on the bias voltage, which can be attributed to an alteration of the structure.

Efficiency enhancement of organic solar cells by fabricating periodic surface textures using direct laser interference patterning.

Direct laser interference patterning (DLIP) is used to fabricate large area, two-dimensional periodic surface patterns on polyethylene terephthalate (PET) substrates to enhance the performance of ZnPc:C60 solar cells by light concentration in the absorber layer. Comparing the power conversion efficiencies to the reference cell on flat PET, a relative increase of 21% is observed for the hexagonal pattern with 0.7 μm period, depicted in the figure.