Changing morphology of BaO/Al2O3 during NO2 uptake and release.

The changes in the morphology of Ba-oxide-based NO(x)() storage/reduction catalysts were investigated using time-resolved X-ray diffraction, transmission electron microscopy, and energy dispersed spectroscopy. Large Ba(NO(3))(2) crystallites form on the alumina support when the catalyst is prepared by the incipient wetness method using an aqueous Ba(NO(3))(2) solution. Heating the sample to 873 K in a He flow results in the decomposition of the Ba(NO(3))(2) phase and the formation of both a monolayer BaO film strongly interacting with the alumina support and nanocrystalline BaO particles.

Effect of barium loading on the desulfation of Pt-BaO/Al2O3 studied by H2 TPRX, TEM, sulfur K-edge XANES, and in situ TR-XRD.

Desulfation processes were investigated over sulfated Pt-BaO/Al2O3 with different barium loading (8 and 20 wt %) by using H2 temperature programmed reaction (TPRX), transmission electron microscope (TEM) with energy dispersive spectroscopy (EDS), sulfur K-edge X-ray absorption near-edge spectroscopy (XANES), and in situ time-resolved X-ray diffraction (TR-XRD) techniques. Both sulfated samples (8 and 20 wt %) form sulfate species (primarily BaSO4) as evidenced by S K-edge XANES and in situ TR-XRD. However, the desulfation behavior is strongly dependent on the barium loading.